Abstract:The aim of this study was to investigate the physical, mechanical, morphological, structural, and thermal properties of polylactic acid (PLA) and polyhydroxybutyrate (PHB) biopolymer composites reinforced with thermally treated wood flour and to determine the formulations having optimum properties by using multi-criteria decision-making (MCDM) methods. As a filler, Scots pine wood flour (untreated and thermally treated at 212 °C) was used at the loading rates of 10% and 30%. The samples were prepared using a twin-screw extruder and then by compression molding. The results showed that the addition of both thermally treated and untreated wood flour slightly increased the density of the composites. According to the color measurement, the thermally treated wood composites were slightly darkened in appearance. In the composites, with both wood fillers, the water absorption and thickness swelling ratios had increased during the 20–250 days of water exposure. Lower water absorption and thickness swelling rates were found for the composites with thermally treated wood filler compared to the other composites. The wood fillers generally lowered the mechanical properties of the PLA and PLA/PHB composites, with the PHB composites as the exception. However, the tensile modulus and Izod impact strength of the composites generally increased with the addition of wood fillers. Morphological examination performed by scanning electron microscopy (SEM) indicated that the wood flour was mostly homogeneously distributed in the matrix, which improved the mechanical properties of the composites. Thermogravimetric analysis (TGA) showed that the addition of wood filler to the neat biopolymers as a rule did not provide significant improvement in the thermal stability; however, the fillers increased the thermal stability of neat PHB. The Fourier-transform infrared (FTIR) spectroscopy detected no differences in the chemical structure of the composites. The X-ray diffraction (XRD) results indicated a general increase in the crystallinity with the addition of wood fillers to the neat biopolymers and the blends. All the findings were subjected to MCDM analysis to determine the formulation having the optimum properties and the results showed this to be the neat PLA sample.

FTIR Spectroscopy Analysis of PLA Biocomposites Reinforced with Hemp Fibers

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Determining the mechanical properties of biomaterial-based economic thermoplastic composites reinforced with hemp fibres

Characterisation of Hemp Fibres Reinforced Composites Using Thermoplastic Polymers as Matrices

Effect of steam explosion and silanization of hemp fibers on polylactic acid biocomposites; analysis of mechanical-thermal properties and fungal biodegradation

Tribological Properties of Hemp Fiber Reinforced Polylactic Acid Bio-Composites: Effect of Different Types of Modification Methods

Fabrication and characterization of polylactic acid/natural fiber extruded composites

The Influence of Chemically Treated Hemp Fibre on the Mechanical Behavior and Thermal Properties of Polylactic Acid Made with FDM

Tensile Strength of Poly(Lactic Acid)/Bleached Short Hemp Fiber Fully Green Composites as Replacement for Polypropylene/Glass Fiber

Thermo-Mechanical Properties of PLA/Short Flax Fiber Biocomposites

Mechanical Performances Analysis and Prediction of Short Plant Fiber-Reinforced PLA Composites

Hemp hurd filled PLA‐PBAT blend biocomposites compatible with additive manufacturing processes: Fabrication, rheology, and material property investigations

Characterization and Scalable Production of Industrial Hemp Fiber Filled PLA Bio-Composites

Polylactic acid and polyhydroxybutyrate coating on hemp fiber: Its effect on hemp fiber reinforced epoxy composites performance

Mechanical Properties and Microstructure of Hemp Hurd Reinforced Polylactide Biocomposites for 3D Printing

Influence of surface treatments and addition of a reactive agent on the properties of PLA/flax and PLA/bamboo composites

Effects of Wet and Dry Treatments on Surface Functional Groups and Mechanical Properties of Flax Fiber Composites

Sustainable jute fiber reinforced polylactic acid composite: Thermochemical and thermomechanical characteristics

Mechanical Properties of PLA Specimens Obtained by Additive Manufacturing Process Reinforced with Flax Fibers

Poly(lactic acid)/flax composites: effect of surface modification and thermal treatment on interfacial adhesion, crystallization, microstructure, and mechanical properties

Interactive Influence of Biofiber Composition and Elastomer on Physico-Mechanical Properties of PLA Green Composites