Abstract:Crevice corrosion of carbon steel was investigated in different exposure environments by performing coupon exposure and electrochemical tests. The extent of corrosion on the bold surface of a carbon steel crevice coupon was more severe at 80 degrees C than at 21 degrees C, in aerated rather than dearated solutions, and with gamma-radiation present. In contrast to normal crevice corrosion, we observed `inverse crevice corrosion' behavior, the phenomenon where it is the corrosion on the bold surface that is accelerated when coupled, rather than that on the crevice surface. The coupling current measured between a crevice and a bold electrode in an electrochemical cell was also negative. This inverse crevice corrosion behavior is attributed to a significantly lower metal cation dissolution capacity of the small occluded water volume in the crevice, compared to that of the bulk water volume over the bold surface. The reduction in dissolution capacity results in faster and earlier formation of a protective oxide layer. Corrosion of the bold and crevice surfaces evolves at different rates, leading to galvanically accelerated corrosion of the bold surface. The effect of.-radiation on corrosion evolution in different solution environments leading to inverse crevice corrosion is discussed. (C) The Author(s) 2017. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution 4.0 License (CC BY, http://creativecommons.org/licenses/by/4.0/), which permits unrestricted reuse of the work in any medium, provided the original work is properly cited. All rights reserved.

Interaction between crevice and galvanic corrosion of X65 carbon steel in the CO2-saturated NaCl solution under the coupling of crevice and galvanic effects

Effect of Crevice Size on Crevice Corrosion of N80 Carbon Steel in CO2-Saturated NaCl-HAc Solution

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

The stress corrosion cracking behavior of N80 carbon steel under a crevice in an acidic solution containing different concentrations of NaCl

Applicability Discussion for Multi-Peak Gaussian Model of Corrosion Layer at Steel/concrete Interfaces

Effect of mechanical stress on electrochemical corrosion of X65 carbon steel in CO2 saturated brine

Galvanic Corrosion Study between Tensile-Stressed and Non-Stressed Carbon Steels in Simulated Concrete Pore Solution

Corrosion Behavior of X65 Steel in Carbon Dioxide Solution under High Temperature and High Pressure

A Comparison Study on the Natural and Half-Soaking Galvanic Accelerated Corrosion of Reinforced Concrete Based on an Improved Electrochemical Model

Crevice Corrosion Behaviors Between CFRP and Stainless Steel 316L for Automotive Applications

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Investigation of Crevice Corrosion Behavior of HRB355 Steel in 3.5% NaCl solution using Coupled multi-electrode arrays

Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive films on X70 micro-alloyed steel

In Situ Electrochemical Monitoring of the Crevice Corrosion Process of the 7075-T651 Aluminium Alloy in Acidic NaCl and NaNO3 Solution

Inverse Crevice Corrosion of Carbon Steel: Effect of Solution Volume to Surface Area

Cross Impact of CO2 Phase and Impurities on the Corrosion Behavior for Stainless Steel and Carbon Steel in Water-Containing Dense CO2 Environments

CO2 corrosion behavior of simulated heat-affected zones for X80 pipeline steel

Investigation of the evolution of an iron carbonate layer and its effect on localized corrosion of X65 carbon steel in CO2 corrosion environments

Effect of Heat Treatment on Crevice Corrosion Behavior of 304 Stainless Steel Clad Plate in Seawater Environment

Galvanic Corrosion Behaviors of X65-316L Bimetal Tube in Simulated Production Water

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions