Abstract:A series of iron oxide catalysts prepared from ferric/ferrous mixed salts were studied to explore the structure–performance relationship for CO2 hydrogenation. The high selectivity to C5+ hydrocarbons (47 %) at a high CO2 conversion (34 %) could be maintained when the initial Fe3+/Fe2+ ratio in preparation varies from 2/1 to 2.5/0.5, while both the CO2 conversion and selectivity to C5+ hydrocarbons show an obvious decline as the ratio deviates from the range. Combined with various characterization results, the volcano-like evolution of CO2 conversion and selectivity to C5+ hydrocarbons is related to the structure and phase transition of the iron oxide catalysts. With the increase of Fe3+/Fe2+ ratio, the catalyst composition gradually changes from Fe3O4 nanoparticles to β-FeOOH nanorods, meanwhile, the size of Fe3O4 nanoparticles decreases. The smaller Fe3O4 nanoparticles could provide higher active surface area for improved reducibility and CO2 adsorption capacity, whereas the presence of β-FeOOH nanorods is not favorable for the reduction and carburization of catalysts. Consequently, the variation of initial phase composition and structure would affect the formation of Hägg iron carbide (χ-Fe5C2) phase during reaction, which has decisive effect on higher hydrocarbons synthesis from CO2 hydrogenation.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the structure - performance relationship of iron oxide catalysts in the carbon dioxide hydrogenation reaction (CO2 hydrogenation), especially the influence of the initial ratio of Fe3+/Fe2+ on the catalytic performance. Specifically, the research aims to reveal the changes in the activity and selectivity of iron oxide catalysts under different Fe3+/Fe2+ ratios in the CO2 hydrogenation reaction, and to explore the relationship between these changes and the catalyst structure and phase transformation. ### Main problems: 1. **Structure sensitivity**: How does the structure of the iron oxide catalyst affect its performance in the CO2 hydrogenation reaction? 2. **Influence of Fe3+/Fe2+ ratio**: How do different initial ratios of Fe3+/Fe2+ affect the composition, structure and catalytic performance of the catalyst? 3. **Selectivity of higher - carbon hydrocarbons**: How to improve the selectivity of C5+ higher - carbon hydrocarbons and the CO2 conversion rate by adjusting the preparation parameters of the catalyst? ### Research background: With the continuous increase in the concentration of CO2 in the atmosphere, reducing CO2 emissions has become an important task for environmental protection. Converting CO2 into fuels and chemicals is a promising technology, which helps to reduce CO2 emissions and promote sustainable development. The CO2 hydrogenation reaction (CO2 hydrogenation) is considered to be one of the effective ways to achieve this goal. Iron - based catalysts have been widely studied because of their relatively high intrinsic RWGS (reverse water - gas shift reaction) and FTS (Fischer - Tropsch synthesis) activities. However, the synthesis methods and parameters of the catalyst will change its structure and chemical properties, thus affecting the formation and stability of the active phase, and ultimately leading to differences in catalytic performance. Therefore, it is of great significance to study the influence of catalyst preparation on its performance. ### Research methods: The author prepared a series of iron oxide catalysts from a mixed salt solution with different Fe3+/Fe2+ ratios by the co - precipitation method, and systematically studied their catalytic performance in the CO2 hydrogenation reaction. The experimental results show that when the initial ratio of Fe3+/Fe2+ is between 2/1 and 2.5/0.5, the catalyst exhibits the highest CO2 conversion rate (34%) and the selectivity of C5+ higher - carbon hydrocarbons (47%). When deviating from this range, the CO2 conversion rate and the selectivity of higher - carbon hydrocarbons decrease significantly. ### Conclusions: 1. **Volcano - type change trend**: The CO2 conversion rate and the selectivity of C5+ higher - carbon hydrocarbons show a volcano - type curve with the change of the Fe3+/Fe2+ ratio, and the optimal ratio is about 2/1. 2. **Structural change**: As the ratio of Fe3+/Fe2+ increases, the composition of the catalyst gradually changes from Fe3O4 nanoparticles to β - FeOOH nanorods, and the size of Fe3O4 nanoparticles decreases. 3. **Formation of active phase**: Smaller Fe3O4 nanoparticles provide a higher active surface area, which is beneficial for CO2 adsorption and reduction; while the presence of β - FeOOH nanorods is not conducive to the reduction and carbonization of the catalyst. 4. **Role of Hägg iron carbide**: The Hägg iron carbide (χ - Fe5C2) formed during the reaction of the catalyst plays a decisive role in the synthesis of higher - carbon hydrocarbons. Through this research, the author not only reveals the structure sensitivity of iron oxide catalysts in the CO2 hydrogenation reaction, but also provides important guiding significance for the design and development of high - performance iron - based catalysts.

Structure sensitivity of iron oxide catalyst for CO2 hydrogenation

Dynamic structural evolution of iron catalysts involving competitive oxidation and carburization during CO 2 hydrogenation

An Introductive Study about CO 2 Hydrogenation into Hydrocarbons Using Iron Catalysts

Mechanistic Insight into Hydrocarbon Synthesis via CO2 Hydrogenation on χ-Fe5C2 Catalysts

Topotactic Transformation of Metal–Organic Frameworks to Iron-based Catalysts for the Direct Hydrogenation of CO2 to Olefins

Enhancing CO 2 hydrogenation performance via the synergistic effects of iron carbides and iron oxides

Size-controlled Synthesis of Hematite -Fe2o3 Nanodisks Closed with (0001) Basal Facets and {11-20} Side Facets and Their Catalytic Performance for CO2 Hydrogenation

CO2 Hydrogenation on Carbides Formed in situ on Carbon-Supported Iron-Based Catalysts in High-Density Supercritical Medium

Selective synthesis of olefins via CO 2 hydrogenation over transition-metal-doped iron-based catalysts

Selectivity control between reverse water-gas shift and fischer-tropsch synthesis in carbon-supported iron-based catalysts for CO 2 hydrogenation

Unraveling the tunable selectivity on cobalt oxide and metallic cobalt sites for CO 2 hydrogenation

CO 2 hydrogenation to olefins on supported iron catalysts: Effects of support properties on carbon-containing species and product distribution

Surface coordinate geometry of iron catalysts: hydrogenation of CO 2 over Fe/TiO 2 prepared by a novel method

Effects of Different Reductive Agents on Zn-Promoted Iron Oxide Phases in the CO2–Fischer–Tropsch to Linear α-Olefins

Fabrication of Transition Metal (Mn, Co, Ni, Cu)‐Embedded Faveolate ZnFe2O4 Spinel Structure with Robust CO2 Hydrogenation into Value‐added C2+ Hydrocarbons

Isolated dual-active Fe-Co sites efficiently promote CO 2 hydrogenation upgrading

Low-temperature CO2 Hydrogenation to Olefins on Anorthic NaCoFe Alloy Carbides.

The relationship between structure and performance of Mo-ZrO2 catalysts in CO2 hydrogenation

Effect of reduction and carburization pretreatment on iron catalyst for synthesis of light olefins from CO hydrogenation

Influence of Reduction Conditions on Structure of Fe/Tio2 Catalyst for Hydrogenation of Carbon Dioxide

Overturning CO2 Hydrogenation Selectivity by Tailoring the Local Electron Density of Ru/CeO2 Catalysts