Is there a relationship between conformational and transport properties of associative polymers in porous media?
Salomao Chissonde,Viralkumar Patel,Madhar Sahib Azad,Japan J. Trivedi
DOI: https://doi.org/10.1016/j.molliq.2024.124953
IF: 6
2024-05-22
Journal of Molecular Liquids
Abstract:This paper delves into the conformational and transport properties of three different associative polymers (C-319, P-329 and D-118) in porous media, focusing on the role of hydrophobicity at varying concentrations. In our latest paper it was reported that at 1000 parts per million (ppm), higher hydrophobic polymers (D-118) display a distinct increase in shear thickening but a decreased extensional viscosity compared to their less hydrophobic counterparts C-319 and P-329. This relationship inverts at 2000 ppm, where an increase in hydrophobicity is associated with a decrease in shear thickening, and extensional viscosity, suggesting extensional rheology of associative polymers could correlate with porous media behavior at higher concentrations but not at lower concentrations. Higher retention was found to be the reason for the higher resistance factor of higher hydrophobic polymers at 1000 ppm whereas at 2000 ppm they have less retention. Is there another phenomenon related to polymer physics that causes this contradiction, and plays a major role during the transport of associative polymeric flow in porous media? This paper aims to answer this question using the combination of extensional rheology and asymmetrical flow field-flow fractionation (AF4). The extensional viscosity of these systems at 1000 ppm are 90 Pa.s, 222 Pa.s and 201 Pa.s. At 2000 ppm, these values are 448 Pa.s, 344 Pa.s, and 196 Pa.s. The shape factor for D-118 was found to be between 0.41 (at 1000 ppm) and 0.20 (at 2000), an indication that the polymer chains are taking the conformation of random coils and spheres at 1000 and 2000 ppm respectively. For C-319 and P-329, respectively, these values are (0.51–0.57) and (0.40–0.49), an indication that they are even more random. It appears that the higher resistance factor shown by D-118 at 1000 ppm is due to the preserved randomness of the polymer chain and amplified Mw despite having the lower extensional viscosity. Contrarily at 2000 ppm, the shape factor was found to be 0.20, an indication that they are compacted. As the compacted polymer chain doesn't stretch, D-118 doesn't appears to get retained significantly at 2000 ppm. C-319 has more flexible chain than P-329 at both concentrations which is the reason why they have higher extensional viscosity and resistance factor. A novel contribution of this work is the elucidation of porous media transport properties of associative polymers, which are intricately tied to the randomness of polymer chains as well as their molecular weight and hydrophobic characteristics. The key novelty of this work is transport properties of the associative polymer in porous media are better delineated by a combination of AF4 and extensional rheology, and retention appears to be related to the randomness of the polymer chain.
chemistry, physical,physics, atomic, molecular & chemical