T. H. Lengyel,Rong Long,P. Schiavone
Abstract:We consider the role of interfacial slippage in the deformation and stress fields near the tip of a plane interface crack occurring between a compressible hyperelastic material and a rigid substrate. Specifically, we draw comparisons between the two limiting cases of ‘no-slip’ (infinitely high friction) and ‘frictionless’ (zero friction) surfaces by performing corresponding asymptotic analyses in the crack-tip region. Our results indicate that for the no-slip case, when the body is subjected to far-field loading, the crack deforms to a wedge-like shape consistent with experimental observations reported in the literature. Moreover, in this case, the wedge angle is shown to be directly related to ratios of various Cauchy stress components on the bonded surface in the near-tip region. Finite-element simulations reveal that the wedge angle also depends on material compressibility and the far-field loading conditions. By contrast, the analysis of the frictionless case reveals that the crack consistently opens into a smooth parabolic shape with a right wedge angle and near-tip stress field dominated by the normal stress at the surface. The results established here can be used as a basis for the understanding of the role of varying degrees of slippage on interfacial cracks.
What problem does this paper attempt to address?
This paper aims to study the influence of interface slip on the deformation and stress field in the near - tip region of the interface crack between a soft elastomer and a rigid substrate. Specifically, the author compared the interface crack behaviors in two extreme cases: "no - slip" (infinitely high friction) and "frictionless" (zero - friction) surfaces. Through the corresponding asymptotic analysis in the crack - tip region, the author explored the influence of different degrees of slip on the interface crack.
### Background of the Paper
Soft elastomers are widely used in coatings and non - structural adhesives, such as pressure - sensitive adhesives. The overall bonding strength between the soft elastomer layer and the relatively rigid substrate is mainly determined by the intrinsic adhesion work per unit area of the contact surface. Recent studies have shown that the strength of soft adhesives is affected by multiple factors, including surface roughness, viscoelasticity, and interface slip. Among them, the influence of interface slip is particularly significant. When the adhesive layer is peeled off from the substrate, insufficient friction may lead to partial slip, thus dissipating energy at the interface. In addition, experimental observations also found that slip also affects the viscoelastic dissipation of the adhesive material during the peeling process.
### Research Methods
To simulate the peeling process, the author considered a plane - strain interface crack that occurs between a soft material and a rigid substrate. During peeling, the interface crack will open and propagate forward under the action of far - field loads. The author assumes that the soft material is elastic, although most soft adhesives are viscoelastic. The focus of the study is on the local deformation field near the crack tip.
### Main Results
1. **No - Slip Condition**:
- When the soft material is subjected to far - field loads, the crack deforms into a wedge shape, which is consistent with the experimental observations in the literature.
- The wedge angle is directly related to the ratio of the Cauchy stress components on the interface.
- Finite - element simulations show that the wedge angle also depends on the compressibility of the material and the far - field load conditions.
2. **Frictionless Condition**:
- The crack always opens into a smooth parabolic shape, and the wedge angle is a right angle.
- The near - tip stress field is mainly dominated by the normal stress on the surface.
### Conclusions
Through detailed asymptotic analysis and finite - element simulations, the author revealed the influence of interface slip on the deformation and stress field in the near - tip region of the interface crack between a soft elastomer and a rigid substrate. These results provide a basis for understanding the effect of different degrees of slip on the interface crack.
### Formula Summary
- **Deformation Gradient**:
\[
F(X,t)=\nabla_X x = \frac{\partial x_i}{\partial X_A}\hat{e}_i\otimes\hat{E}_A
\]
- **First Piola - Kirchhoff Stress Tensor**:
\[
P=\frac{\partial\psi}{\partial F}=2F\frac{\partial\psi}{\partial C}=P_{iA}\hat{e}_i\otimes\hat{E}_A
\]
- **Cauchy Stress Tensor**:
\[
\sigma = J^{-1}PF^T=\sigma_{ij}\hat{e}_i\otimes\hat{e}_j
\]
- **Asymptotic Solutions**:
- **Frictionless Condition**:
\[
x_1(r,\theta)=\bar{x}_1+br\cos(\theta)+O(r)
\]
\[
x_2(r,\theta)=ar^{1/2}\sin\left(\frac{\theta}{2}\right)+O(r)
\]
- **No - Slip Condition**:
\[
x_1(r,\theta)=a_1r^{1/2}\sin\left(\frac{\theta}{2}\right)+r\cos(\theta)+O(r)
\]
\[
x_2(r,\theta)=a_2r^{1/2}\sin\left(\frac{\theta}{2}\right)+O(r)