Abstract:In this work, we reported that the fibrous silica nanosphere, also called as KCC-1, was facilely synthesized by the improved microemulsion hydrothermal fabrication strategy. The obtained KCC-1 was investigated as the support of the Ni based catalysts toward CO2 methanation. The obtained catalysts with unique dendrimeric mesopore structure and outstanding structural properties could provide easily accessible as well as highly dispersed Ni nanoparticles to the gaseous reactants. Besides, the Ni based catalysts with commercial SiO2 and MCM-41 as supports were also prepared as the reference catalysts to demonstrate the advantages of the dendrimeric mesoporous channels. Various techniques, such as X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), H-2 temperature programmed reduction (H-2-TPR), CO2 temperature programmed desorption (CO2-TPD), X-ray photoelectron spectroscopy (XPS), etc., were used to characterize the catalytic supports and corresponding catalysts. It was found that the metallic Ni nanoparticles could be highly dispersed over the catalysts supported on fibrous KCC-1 with dendrimeric mesoporous channels. Furthermore, the catalytic performances toward CO2 methanation had been further evaluated over these catalysts at different temperatures. It was found that the KCC-1 supported catalyst performed much higher low-temperature catalytic activities than the reference catalysts supported on commercial SiO2 and MCM-41, suggesting that the fibrous and dendrimeric mesoporous channels displayed distinctive advantages by accommodating enough metallic Ni active sites. The kinetic study also revealed that the topology of the mesoporous channel could obviously influence the apparent activation energy in the CO2 methanation reaction. Besides, the temperature programmed surface reaction (TPSR) and in-situ Diffused Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) of the CO2 methanation were also carried out to reveal the possible reaction pathway and mechanism. We also found that the fibrous silica nanosphere (KCC-1) supported catalyst demonstrated much better sintering-proof property of the metallic Ni nanoparticles than the reference catalysts during the 40 h stability tests at 400 degrees C. Therefore, the present fibrous silica nanosphere (KCC-1) could be considered as the promising support for Ni based catalysts toward CO2 methanation.

Synthesis, characterization and activity pattern of carbon nanofibers based copper/zirconia catalysts for carbon dioxide hydrogenation to methanol: Influence of calcination temperature

Structural Evolution and Catalytic Properties of Nanostructured Cu/Zro2 Catalysts Prepared by Oxalate Gel-Coprecipitation Technique

CO2 Hydrogenation to Methanol over Cu/ZnO/ZrO2 Catalysts Prepared Via a Route of Solid-State Reaction

Copper nanoparticles encapsulated in zeolitic imidazolate framework-8 as a stable and selective CO2 hydrogenation catalyst

Synergistic effect of zirconia oxygen vacancies and Cu nanoparticles on catalytic conversion of CO2 to CO at low temperatures

Influences of preparation methods of ZrO2 support and treatment conditions of Cu/ZrO2 catalysts on synthesis of methanol via CO hydrogenation

Catalytic Chemical Vapor Deposition of Methane to Carbon Nanotubes: Copper Promoted Effect of Ni/MgO Catalysts

Optimization of bi-metallic (Fe–Co) catalyst on kaolin support for carbon nanofiber growth in a CVD reactor

Synthesis and evaluation of novel Cu-based adsorbent-containing catalysts for CO 2 hydrogenation to methanol and value-added products

Synthesis, characterization and activity pattern of Cu–ZnO/ZrO2 catalysts in the hydrogenation of carbon dioxide to methanol

Insights on the Highly Stable and Coke-Resistant Nickel/Zirconia Nanocatalyst for the Methanation of Carbon Dioxide

Ni-based catalysts derived from Ni-Zr-Al ternary hydrotalcites show outstanding catalytic properties for low-temperature CO<sub>2</sub> methanation

Optimization and understanding of ZnO nanoarray supported Cu-ZnO-Al2O3 catalyst for enhanced CO2 -methanol conversion at low temperature and pressure

Effect of Catalyst Synthesis Parameters on the Performance of CO2 Hydrogenation to Methanol over SBA-15 Supported Cu/ZnO-Based Catalysts

Surface active structure of ultra-fine Cu/ZrO2 catalysts used for the CO2+H2 to methanol reaction

Constructing Highly Dispersed Ni Based Catalysts Supported on Fibrous Silica Nanosphere for Low-Temperature CO2 Methanation

Zn-incorporated joule-heated carbon nanofiber aerogel-supported Cu catalyst for hydrogen production via methanol steam reforming

NiFe and CoFe nanocatalysts supported on highly dispersed alumina-silica: Structure, surface properties, and performance in CO2 methanation

Highly Active CNT-Promoted Cu–ZnO–Al2O3 Catalyst for Methanol Synthesis from H2/CO/CO2

Methanol Synthesis from CO2 Hydrogenation with a Cu/Zn/Al/Zr Fibrous Catalyst

CO2 Methanation over Nickel-Based Catalysts Supported on MCM-41 with in Situ Doping of Zirconium