Abstract:Liquid crystalline elastomers (LCEs) can show reversible shape change when the materials go through isotropic-liquid crystal phase transition (T-i). To get such actuation, LCEs have to be aligned into monodomain samples, in which the mesogens are orientated more or less in a uniform direction. Normally, LCEs are covalently cross-linked, which makes the alignment very difficult. We have previously shown that this problem can be solved by designing LCEs with exchangeable links. The material for demonstration was synthesized by reacting an epoxy-terminated biphenyl mesogen with sebacic acid in the presence of triazobicyclodecene catalyst for transesterification. The resultant material is in fact a liquid crystalline vitrimer. When the material is stretched above the topology freezing transition temperature (T-v), the accelerated transesterification reaction allows topology adjustment. The alignment can be fixed by cooling afterwards. However, as the T-i is very close to T-v in this sample, it is easy for the alignment to disappear when the temperature increases to above T-i to trigger the actuation. This not only limits the operating temperature range, but also destroys the alignment after multiple heating-cooling cycles. Consequently, it is desirable to increase the distance between T-i and T-v by reducing T-i. To this end, a second epoxy-terminated cyanostilbene mesogen (EP11) was added into the main chain of the liquid crystalline vitrimer. The result shows that the copolymerization of the two types of mesogens can effectively decreases T-i without affecting the T-v too much. It broadens the range between T-i and T-v. The more EP11, the lower T-i. When the content of EP11 is 20 mol%, T-i is 82 degrees C, which is 31 degrees C lower than the previous liquid crystalline vitrimer. The copolymer can also be used to make into monodomain LCE by stretching at high temperature. The resultant monodomain LCE has a similar reversible elongation-contraction actuation ratio as the previous liquid crystalline vitrimer. More importantly, the large distance between T-i and T-v makes it possible to trigger the actuation by heating it to a temperature of 15 degrees C above T-i without destroying the alignment. Little fatigue has been identified after repeating the reversible elongation-contraction actuation for 120 times.

Voxelated liquid crystal elastomers

Soft actuators based on liquid-crystalline elastomers.

Layered liquid crystal elastomer actuators

Micron-sized Liquid Crystalline Elastomer Actuators

Liquid Crystal Elastomer Actuators from Anisotropic Porous Polymer Template.

Repeatedly Programmable Liquid Crystal Dielectric Elastomer with Multimodal Actuation.

Mouldable Liquid-Crystalline Elastomer Actuators with Exchangeable Covalent Bonds

Vacuum Thermoforming of Optically Switchable Liquid Crystalline Elastomer Spherical Actuators

Monolithic shape-programmable dielectric liquid crystal elastomer actuators

Structure-induced Intelligence of Liquid Crystal Elastomers.

Electrostatically Powered Multimode Liquid Crystalline Elastomer Actuators

3D Microstructures of Liquid Crystal Networks with Programmed Voxelated Director Fields

Guided Folding of Nematic Liquid Crystal Elastomer Sheets into 3D via Patterned 1D Microchannels

A Liquid Crystalline Vitrimer with Better Actuation Repeatability

Low-Voltage-Driven Actuators Using Photo-Cross-Linked Ionic Columnar Liquid-Crystalline Polymer Films

Locking Alignment of Liquid Crystal Actuators Using Hydrogen Bonds to Enable Room‐Temperature Shape Programmability and Enhanced Work Capacity

Shape-programmable liquid crystal elastomer structures with arbitrary three-dimensional director fields and geometries

Three-Dimensional Blueprinting of Molecular Patterns in Liquid Crystalline Polymers

Liquid crystal elastomer shells with topological defect-defined actuation: Complex shape morphing, opening/closing, and unidirectional rotation

Elastomers Grow into Actuators

Photo- and Humidity-Responsive Liquid Crystal Copolymer Actuators Fabricated via Vapor-Assisted Alignment