Microstructure, Nanoindentation and Corrosion Behavior of Colmonoy-5 Deposition on SS410 Substrate Using Laser Cladding Process

Sundara Subramanian Karuppasamy,N. Jeyaprakash,Che-Hua Yang

DOI: https://doi.org/10.1007/s13369-021-06398-6

IF: 2.807

2022-01-06

Arabian Journal for Science and Engineering

Abstract:Stainless steel 410 (SS410) is majorly used in manufacturing the components of gas turbines, pump shafts, thermal power plants, safety valves, and reactor core components that operate in severe aggressive environments. Prolonged exposure of these critical components in such environments results in reduction in their mechanical properties like tensile strength, hardness, wear, and corrosion resistance thereby causing failures and property losses. The present study is aimed to enhance the corrosion resistance behavior of SS410 by depositing the Colmonoy-5 alloy particles by means of laser cladding technique. The microstructure and hardness studies were carried out to reveal the formation of structure and improvement in hardness, respectively. Further, the corrosion analysis was performed on both the base and cladded samples in different duration with the test solution made from 3.5 wt% NaCl. Then, the corroded surface morphology and their corresponding roughness were analyzed. The results showed that the existence of the floret-shaped structure was observed on the cladded surface and improved the hardness due to the presence of chromium borides and carbides in the γ-nickel matrix. Among the various duration, the 8 h cladded sample exhibits high resistance to corrosion due to the formation of finite passivation film made by Cr-rich borides. In addition to that, the reduced surface roughness was observed on the 8 h cladded sample when compared with the base and other clad samples.

multidisciplinary sciences