Abstract:Ice formation and accumulation on surfaces can result in severe problems for solar photovoltaic installations, offshore oil platforms, wind turbines and aircrafts. In addition, blockage of pipelines by formation and accumulation of clathrate hydrates of natural gases has safety and economical concerns in oil and gas operations, particularly at high pressures and low temperatures such as those found in subsea or arctic environments. Practical adoption of icephobic/hydrate-phobic surfaces requires mechanical robustness and stability under harsh environments. Here, we develop durable and mechanically robust bilayer poly-divinylbenzene (pDVB)/poly-perfluorodecylacrylate (pPFDA) coatings using initiated chemical vapor deposition (iCVD) to reduce the adhesion strength of ice/hydrates to underlying substrates (silicon and steel). Utilizing a highly-cross-linked polymer (pDVB) underneath a very thin veneer of fluorine-rich polymer (pPFDA) we have designed inherently rough bilayer polymer films that can be deposited on rough steel substrates resulting in surfaces which exhibit a receding water contact angle (WCA) higher than 150° and WCA hysteresis as low as 4°. Optical profilometer measurements were performed on the films and root mean square (RMS) roughness values of Rq = 178.0 ± 17.5 nm and Rq = 312.7 ± 23.5 nm were obtained on silicon and steel substrates, respectively. When steel surfaces are coated with these smooth hard iCVD bilayer polymer films, the strength of ice adhesion is reduced from 1010 ± 95 kPa to 180 ± 85 kPa. The adhesion strength of the cyclopentane (CyC5) hydrate is also reduced from 220 ± 45 kPa on rough steel substrates to 34 ± 12 kPa on the polymer-coated steel substrates. The durability of these bilayer polymer coated icephobic and hydrate-phobic substrates is confirmed by sand erosion tests and examination of multiple ice/hydrate adhesion/de-adhesion cycles.

Durability of Lubricated Icephobic Coatings under Various Environmental Stresses

Durability enhancement of low ice adhesion polymeric coatings

Self-regulated Secretory Materials for Long-Term Icephobicity

Icephobicity and electrical assessment of slippery coating impregnated with a stabilized hydroxyl-terminated lubricant for high voltage insulation application

Scalable and durable polymeric icephobic and hydrate-phobic coatings

Durable One-Component Polyurea Icephobic Coatings with Energy-Saving Performance in Electrical Heating De-Icing

Manufacturing and Icephobic Performance Evaluation of Cold-Sprayed Adhesive Perfluoroalkoxy Alkane Coatings

Durable anti-icing coating with stability based on self-regulating oil storage layer

Icephobic Coating Based on Epoxy/Polydimethylsiloxane Interpenetrating Polymer Network Gel

Mechanically Robust Liquid-Embedded Coating with Anti-Icing/deicing Durability

Anti-icing performance of hydrophobic coatings on stainless steel surfaces

Icephobic performance of one-step silicone-oil-infused slippery coatings: Effects of surface energy, oil and nanoparticle contents

Facile Fabrication of Robust Superhydrophobic Ice Shedding Coating with Superior Corrosion Resistance and Temperature Durability

On the Durability of Icephobic Coatings: A Review

Facilely Fabricated Self-Lubricated Photothermal Coating with Long-Term Durability and External-Replenishing Property for Anti-Icing/Deicing.

Hydro- and Icephobic Properties and Durability of Epoxy Gelcoat Modified with Double-Functionalized Polysiloxanes

Durable and Scalable Candle Soot Icephobic Coating with Nucleation and Fracture Mechanism

Transparent Liquid-like Slippery Coating with Excellent Photothermal Performance and Durability for Anti-/De-Icing Applications

Icephobic coatings beyond boundaries: Layered integration of phase change materials beneath a PEG-PDMS copolymer–containing coating to enhance anti-icing performance

Robust polyurea icephobic coatings with static large-scale de-icing and dynamic anti-icing performance

Durable solid lubricant wind turbine blade anti-icing coating based on saturated chain polyhydrocarbons