Abstract:We report the synthesis of hybrid thin films based on polymethyl methacrylate) (PMMA) and polystyrene (PS) doped with 1%, 3%, 5%, and 7% of cerium dioxide nanoparticles (CeO2 NPs). The As-prepared thin films of (PMMA-PS) incorporated with CeO2 NPs are deposited on a glass substrate. The transmittance T% (λ) and reflectance R% (λ) of PMMA-PS/CeO2 NPs thin films are measured at room temperature in the spectral range (250–700) nm. High transmittance of 87% is observed in the low-energy regions. However, transmittance decreases sharply to a vanishing value in the high-energy region. In addition, as the CeO2 NPs concentration is increased, a red shift of the absorption edge is clearly observed suggesting a considerable decrease in the band gap energy of PMMA-PS/CeO2 NPs thin film. The optical constants (n and k) and related key optical and optoelectronic parameters of PMMA-PS/Ce NPs thin films are reported and interpreted. Furthermore, Tauc and Urbach models are employed to elucidate optical behavior and calculate the band gaps of the as-synthesized nanocomposite thin films. The optical band gap energy of PMMA-PS thin film is found to be 4.03 eV. Optical band gap engineering is found to be possible upon introducing CeO2 NPs into PMMA-PS polymeric thin films as demonstrated clearly by the continuous decrease of optical band gap upon increasing CeO2 content. Fourier-transform infrared spectroscopy (FTIR) analysis is conducted to identify the major vibrational modes of the nanocomposite. The peak at 541.42 cm−1 is assigned to Ce–O and indicates the incorporation of CeO2 NPs into the copolymers matrices. There were drastic changes to the width and intensity of the vibrational bands of PMMA-PS upon addition of CeO2 NPs. To examine the chemical and thermal stability, thermogravimetric (TGA) thermograms are measured. We found that (PMMA-PVA)/CeO2 NPs nanocomposite thin films are thermally stable below 110 °C. Therefore, they could be key candidate materials for a wide range of scaled multifunctional smart optical and optoelectronic devices.

Three-Dimensional Ordered CeO2 Hollow Spheres (3DOHSs-CeO2) from Polymethylmethacrylate/CeO2 Core/Shell Microsphere Colloidal Crystals

Deposition of Sm2O3 doped CeO2 thin films from Ce(DPM)4 and Sm(DPM)3 (DPM=2,2,6,6-tetramethyl-3,5-heptanedionato) by aerosol-assisted metal–organic chemical vapor deposition

Facile One-Step Synthesis of Double-Shelled CeO2 Hollow Spheres and Their Optical and Catalytic Properties

Facile Synthesis of Well-Defined CeO2 Hollow Spheres with a Tunable Pore Structure

Controllable Template-Free Hydrothermal Synthesis of 3D Porous CeO2 Hollow Nanospheres and Their Optical Performances

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Use of Carbonaceous Polysaccharide Microspheres As Templates for Fabricating Metal Oxide Hollow Spheres

Study of the Preparation and Properties of CeO2single/multiwall Hollow Microspheres

Synthesis of poly(methacrylic acid)-manganese oxide dihydroxide/silica core-shell and the corresponding hollow microspheres

Hierarchically mesostructured doped CeO2 with potential for solar-cell use

ZnO-Based Hollow Microspheres: Biopolymer-Assisted Assemblies from ZnO Nanorods

Self-template hydrothermal synthesis of CeO2 hollow nanospheres

Solvthermal Synthesis of CeO<sub>2</sub> Hollow Nanospheres

Co(3)O(4)@CeO(2) core@shell cubes: designed synthesis and optimization of catalytic properties.

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Co3O4@CeO2 Core@Shell Cubes: Designed Synthesis and Optimization of Catalytic Properties

Synthesis, Optical, Chemical and Thermal Characterizations of PMMA-PS/CeO2 Nanoparticles Thin Film

Template-Free Synthesis Of Single-Crystalline-Like Ceo2 Hollow Nanocubes

Self-Organized Monolayer of Nanosized Ceria Colloids Stabilized by Poly(vinylpyrrolidone)