Long-term outdoor weathering evaluation of wood plastic composites

Liqing Wei,Jed Cappellazzi,Mark Manning,Armando G. McDonald,Skyler Foster,Jeffrey J. Morrell

DOI: https://doi.org/10.1007/s00107-021-01762-7

2021-10-30

European Journal of Wood and Wood Products

Abstract:There are relatively few long-term studies of wood plastic composite (WPC) performance, especially under harsh sub-tropical conditions. This study examined changes in wood/polymer composition, surface chemistry, and thermal properties of WPC decking with and without a co-extruded cap layer after 8–14 years of above ground outdoor exposure at a sub-tropical site near Hilo, Hawaii. WPC condition was assessed using combinations of destructive and non-destructive (TGA, DSC, and FTIR spectroscopy) methods with WPC wood content determined after chemical digestion. Coextruded WPCs were more resistant to above ground weathering than uncapped materials possibly because the cap layer reduced oxygen availability at the interface between the inner (core) and outer (cap) layer. Moreover, increased vinyl concentrations coupled with lower degrees of crystallinity of the polymer matrix suggested the chain crosslinking and scission reactions occurred simultaneously. Wood components in the cap layer of the coextruded WPCs were less susceptible to weathering due to the encapsulation by plastic. Therefore, the cap layer showed relatively better thermal stability than the uncapped WPCs.

materials science, paper & wood,forestry