Abstract:Admixture and water-cement ratio are important factors affecting the development of properties of cement mortar or concrete. In order to study the influence of admixtures and water-cement ratio on the hydration products and the mechanical properties of cement-based materials, the study combined hydration reaction mechanism of pure cement and silicate admixture, derived the formulae of hydration products, theoretical maximum mixing amount and total porosity of composite cement-based materials, and investigated the effects of mixing amount of cement mortar with fly ash, steel slag and lithium slag on total porosity, mechanical properties and hydration products. This paper designed 3 gradients of water-cement ratio (0.50, 0.42 and 0.34), 3 kinds of admixtures (lithium slag, fly ash and steel slag) and 2 contents (20% and 60%); the ratio of cementitious material to sand was 1:2.5, and then, molding specimen accorded with the mix of mortar in the triple mold and the mechanical properties of mortar were tested when specimen was cured to 1, 3, 7, 28 and 90 d. The results showed that, after the same content of fly ash, steel slag and lithium slag incorporation, the contents of hydration products of composite cementitious materials, i.e. calcium hydroxide (CH) and calcium silicate hydrate (CSH), and the total porosity were smaller than those of pure cement; when the water-cement ratio decreased from 0.50 to 0.34, the total porosity of cement mortar decreased from 16.0% to 9.3%, and the contents of CH and CSH increased for the compound cement-based materials with mixing amount of 5%, but the increments were not big; the porosity of fly ash, steel slag and lithium slag cement-based composite materials reduced from 16.6%, 17.2% and 16.0% to 9.9%, 10.9% and 9.3%, respectively. When the admixture amount increased to 10%, the variation of porosity and hydration products of the 3 kinds of mortar was different. The content of hydration products (CH and CSH) of composite cementitious materials was still smaller than that of pure cement. Compared to pure cement, the contents of CH and CSH of lithium slag mortar reduced by about 81.1% and 4.2%, fly ash mortar reduced by about 20.9% and 9.5%, and steel slag mortar reduced by approximately 3.0% and 9.5%, respectively. The porosity of lithium slag, fly ash and steel slag mortar increased by 0.1%, 3.6% and 7.6%, respectively. Among the 3 kinds of admixtures, the theoretical maximum mixing amount of fly ash was the maximum, followed by lithium slag, and the steel slag’s theoretical maximum mixing amount was the minimum. It was found that the compressive strength of lithium slag cement-based composite material was prior to fly ash and steel slag cement-based composite materials. In early stage (14 days ago), the compressive strength of fly ash mortar was prior to steel slag mortar; when water-cement ratio was relatively high, the compressive strength of steel slag mortar was close to fly ash. When the mixing amount was 20%, the compressive strength of lithium slag cement mortar was prior to pure cement mortar; if the mixing amount was 60%, the compressive strength of fly ash, steel slag and lithium slag mortar was worse than pure cement mortar. The study provides theoretical basis for material adding in mortar and concrete.

The influence of mineral admixtures on bending strength of mortar on the premise of equal compressive strength

The Synergy Effect of Limestone Powder and Mineral Admixtures on the Mechanical Property of Mortar

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Influence of Mineral Admixtures on Physical Properties and Pore Structure of Dry-Mixed Mortars

Rheological properties of mortar and concrete with low binder content

Influence of admixture and water-cement ratio on hydration products and mechanical properties of cement-based materials

Influences of Fly Ash, Slag and Silica Fume on Cement Mortar Fluidity and Early Strength

Effect of mineral admixtures on drying and autogenous shrinkage of concrete with low water-to-binder ratio

Influence of Mineral Admixtures on Strength Development of Basalt Fiber Reinforced Cement Mortar

Effects of Mineral Admixture on Properties of Young Concrete

Effect of mineral admixtures on the hydration heat of mortar in super high strength concrete

Stuay of Mineral Admixtures as Fine Aggregate on Hydration Products and Spectral Performance of Mortar

Rheological Behavior and Strength Characteristics of Cement Paste and Mortar with Fly Ash and GGBS Admixtures

Influence of Mineral Admixtures on Compressive Strength and Pore Structure of Steam-Cured High-Strength Cement Paste

Effect of Mineral Admixtures on Compressive Strength of Lytag Concrete

Influence of Mineral Admixtures on the Characteristics of Steam Curing Hardened Cement Paste

Effects and Mechanisms of Mineral Admixtures on Sulfate Attack of Cement Mortars

Influence of superplasticizers and mineral admixtures on the workability of mortar at low water-binder ratio

Effect of mineral admixtures on resistance to chemical attack of blended mortar

Influence of High-Volume Mineral Mixtures and the Steam-Curing Temperatures on the Properties of Precast Concrete

Effect of steel slag powder, fly ash, and silica fume on the mechanical properties and durability of cement mortar