Preparation of magnetic chitosan microspheres by combining membrane emulsification and in-situ method
Han ZHANG,Li-xia SUN,Li-qin ZHOU,Yun ZOU,Yu WEI,Cai-zhen LUO,Jia-da NIE,Jun WU,Ye-pei YANG,Dan-kui LIAO
DOI: https://doi.org/10.13624/j.cnki.issn.1001-7445.2016.1870
2017-01-01
Abstract:In order to prepare the magnetic chitosan microspheres with uniform particle size, SPG membrane emulsification and in-situ method were effectively combined. The membrane emulsification pressure, the content of the emulsifier, the disperse phase ratio, the stirring rate, the content of the crosslinking agent, the pH condition of the solution, and the mass ratio of chitosan to FeCl2 ·4H2 O were investigated. The optimal conditions were as follows: the acetic acid of 3%, emulsifier Span-80 content of 4 mL, emulsification pressure of 200 kPa, speed of 400 r/min, glutaraldehyde of 2 mL, solution pH of 7. 5, mass ratio of chitosan to FeCl2 ·4H2 O of 1:1. Under these conditions, the magnetic chitosan microspheres with average particle diameter of 6. 78 μm and saturation magnetization of 25. 69 emu/g were obtained. The uniform magnetic microspheres could be produced by the membrane emulsification combining in-situ method. Due to the easy operations and the mild conditions, this method displays great potential in the preparation of magnetic micro-spheres.