Fabrication and formation studies on single-walled CA/NaCS-WSC microcapsules

qingxi wu,dongqiang lin,shanjing yao

DOI: https://doi.org/10.1016/j.msec.2015.10.090

2016-01-01

Abstract:The micron-sized calcium alginate/sodium cellulose sulfate-water soluble chitosan (CA/NaCS-WSC) microcapsules were prepared by membrane emulsification method using sodium alginate (NaAlg), NaCS and WSC as raw materials. The CA/NaCS microspheres prepared dispersed well and held spherical shape with an emulsifier volume ratio of 7:3 (Span 80:Tween 80) and a concentration of cross-linking agent of 1.5% (w/v) calcium chloride and 5% (w/v) sodium chloride. The CA/NaCS-WSC microcapsules had a spherical shape with average diameter of 62.36 +/- 13.87 pm. A fluorescent ring could be seen obviously on the surface of CA/NaCS-WSC microcapsules under confocal microscope, when WSC was labeled by fluorescein isothiocyanate. The discussion on the formation studies implied that Ca2+ could diffuse into the droplets of NaAlg/NaCS forming CA/NaCS microspheres, while NaCS.could react with WSC forming a polyelectrolyte complexes film. The microcapsules prepared with typical wall-capsule/core structure could be used to develop micron-sized drug delivery carriers. (C) 2015 Elsevier B.V. All rights reserved.