Investigation of Mechanical Properties and Color Changes of 3D-Printed Parts with Different Infill Ratios and Colors After Aging
Oğuz Koçar,Nergizhan Anaç,Erhan Baysal,Furkan Parmaksız,İrfan Akgül
DOI: https://doi.org/10.3390/ma17235908
IF: 3.4
2024-12-04
Materials
Abstract:Since their inception, plastics have become indispensable materials. However, plastics used for extended periods in industrial applications are prone to aging, which negatively impacts their material behavior and performance. To ensure the long-term usability of these materials, they must be tested in real-time, in-service environments to assess degradation. In practice, however, accelerated aging techniques are commonly employed to avoid time loss. Over time, various indicators of degradation in plastics emerge, such as changes in molecular weight, cracking, and mechanical properties like strain at break and impact strength. Among these, color deterioration or change is a critical factor that helps evaluate the service life of these materials. Considering the increasing use of plastics in 3D printing today, and the growing focus on strength over aesthetics in these applications, it is particularly useful to evaluate aging in plastics based on the relationship between color and strength. The wide application of 3D printing in various industries necessitates understanding material properties under aging conditions. This study examines the effects of aging on the mechanical behavior of polylactic acid (PLA) with three different colors (yellow, orange, and red) and three different infill ratios (20%, 60%, and 100%). The samples underwent an accelerated aging process of 432 h, which included 8 h of UV radiation, 15 min of water spraying, followed by 3 h and 45 min with the UV lamps turned off. Tensile tests, bending tests, hardness measurements, and color evaluations were conducted on the samples, linking the color changes after aging with the materials' mechanical properties. The results show that after aging, yellow samples with a 100% infill ratio exhibited a 6.9% increase in tensile strength (44.50 MPa to 47.58 MPa). Orange samples with a 100% infill ratio were less affected by aging, while red samples experienced a decrease in tensile strength across all infill ratios. Regarding bending force, increases were observed in the orange, yellow, and red samples by 10.37%, 25.05%, and 8.87%, respectively. This study underscores the importance of color selection when designing 3D-printed materials for long-term applications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering