Unraveling the Formation Mechanism of a Hybrid Zr-Based Chemical Conversion Coating with Organic and Copper Compounds for Corrosion Inhibition
Xiaoyang Liu,Donald Vonk,Kim Kisslinger,Xiao Tong,Gary Halada,Stanislas Petrash,Kate Foster,Yu-chen Karen Chen-Wiegart
DOI: https://doi.org/10.1021/acsami.0c19203
2021-01-19
Abstract:Environmentally friendly chromate-free, zirconium (Zr)-based conversion coating is a promising green technology for corrosion protection. Additives in the surface treatment provide critical functionalities and performance improvements; however, mechanistic understanding as to how the additives influence the coatings remains unclear. In this study, a new organic–inorganic hybrid Zr-based conversion coating combines copper (Cu) compounds and polyamidoamine (PAMAM), taking advantage of the complementary nature of organic and inorganic additives. A multimodal approach combining electron and X-ray characterization is applied to study the interaction of Cu<sup>2+</sup> and PAMAM and the resulting impacts on coating formation. Adding PAMAM changed the surface morphology, thickness, distribution of Cu in the clusters, and void formation of the coatings. High PAMAM (100–200 ppm) leads to little conversion coating formation, and low PAMAM (0–25 ppm) shows voids formation under the coatings. Moreover, PAMAM incorporates in the coating in the form of a PAMAM–Cu complex with a higher concentration toward the surface, providing an organic layer at the surface of the coating. X-ray absorption near-edge structure (XANES) spectroscopy shows the difference between the conventional and the hybrid coating treatments in an alkaline solution to simulate the E-coat process, suggesting the contribution of PAMAM in the enhanced chemical stability in an alkaline environment. Therefore, an intermediate range of addition of PAMAM (50 ppm) is optimal to (1) avoid excessive voids formation, (2) promote some Cu cluster formation and thus enhance the Zr-based coating formation, and (3) incorporate organic components into the coating to improve the adhesion of the subsequent coatings. Overall, this work furthers our knowledge on the formation mechanism of an effective and environmentally friendly hybrid conversion coating for corrosion inhibition, demonstrating a critical processing–structure–property relationship. This study will benefit future development of green and effective surface treatment technology.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c19203?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c19203</a>.Surface chemical composition of pristine Fe thin film, surface morphology and Cu elemental distribution of F-P50 sample on the surface and cross-section showing Cu-rich clusters, quantification of the size and number density of the clusters as a function of PAMAM concentration, surface morphology of the Zr-based conversion coatings without Cu<sup>2+</sup> and PAMAM, STEM/EDS maps analysis of the coatings on cold rolled steel substrate, STEM/EDS maps analysis of sample F-P200, Cu to Zr atomic ratio in the clusters in samples F-P0 and F-P50, quantification of the atomic ratio distribution in the surface cluster, fitting parameters of Cu 2p3/2 XPS in samples F-P0, F-P50 and F-P100and surface Zr XPS peaks of different samples (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c19203/suppl_file/am0c19203_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology