Abstract:The material accumulation during roasting in the practical production causes the hypoxia of the internal materials, leading to the relatively lower vanadium recovery than that in theoretical studies. This work aims to solve the problem of material hypoxia through the Na2O2-briquetting roasting route. The vanadium slag and Na2O2 powders were mixed, briquetted, and roasted at various parameters. The generated phases and their distributions were analyzed using X-ray diffraction, Fourier transform infrared spectroscopy, and electron probe microanalysis. The analyzing results showed that Fe2O3, Fe3O4, Mg0.165Mn0.835O, CaTiO3, and Na3VO4 were generated during roasting. The solid–solid reaction between V2O5 and Na2O was described using the vacancy-mediated diffusion mechanism. Na+ (or V5+), in the Na2O (or V2O5) layer, jumped and diffused through the Na+ (or V5+) vacancies (in the Na3VO4 layer) to the Na3VO4/V2O5 (or Na3VO4/Na2O) interface. Na+ (or V5+) reacted with V2O5 (or Na2O) and O2 decomposed from Na2O2 or transported from the air to generate Na3VO4. The roasted mixture was leached in an aqueous solution to study the effects of the roasting variables on the vanadium leaching recovery. The vanadium leaching recovery was very sensitive to the roasting variables, it showed very complicated relationships with the Na/V molar ratio, temperature, time, and briquetting pressure. The maximum vanadium leaching recovery of 95.57 pct was achieved when the Na/V molar ratio, temperature, time, and pressure were optimized as 3/1, 850 °C, 2.5 hours, and 5 MPa, respectively. The leaching solution containing vanadium was processed via precipitation and calcination to gather vanadium. The obtained compound was identified as V2O5 with a purity of 96.84 pct, based on the high consistency of diffraction peaks between the present work and that of the joint committee on powder diffraction standards.

Extraction of Vanadium Powder by Metallothermic Reduction

Direct Reduction of Solid V2O5 with Hydrogen at 600–1400 °C

Preparation of high purity vanadium

High-Efficiency Extraction of Fe, V, and Ti from Vanadium Titano-Magnetite Concentrate Based on Activated Reduction

A Method to Extract Vanadium from HIsmelt Reduction Slag: In Situ Sodium Salt Oxidation and Alkali Leaching

Recovery of Vanadium from Carbonated Solution by Extraction with Transformed Aliquat 336 and Stripping-Precipitation

An extraction process to recover vanadium from low-grade vanadium-bearing titanomagnetite

Microwave-hydrogen synergistic reduction of vanadium titano-magnetite

Extraction of Vanadium From Vanadium Slag Through a New Technique Route Including Na2O2-Briquetting Roasting Process

Vanadium extraction from water-cooled vanadium converter slag via salt-free roasting and acid leaching

Cleaner and effective extraction and separation of iron from vanadium slag by carbothermic reduction-chlorination-molten salt electrolysis

Recovery of Valuable Elements from Molten Vanadium Slag Through High-Temperature Reduction

Study of V<sub>2</sub>O<sub>5</sub> Direct Alloying Reductants

Thermodynamic studies on gas-based reduction of vanadium titano-magnetite pellets

Extraction of Vanadium from CaO–SiO2–MgO–Al2O3 Slags Based on Vaporization of Vanadium Pentoxide

Cleaner extraction of vanadium from vanadium-chromium slag based on MnO2 roasting and manganese recycle

Kinetic Studies on Gas-Based Reduction of Vanadium Titano-Magnetite Pellet

High efficiency extractions of V, Cr, Ti, Fe and Mn from vanadium slag by microwave heating

Thermodynamic study of direct reduction of high-chromium vanadium–titanium magnetite (HCVTM) based on phase equilibrium calculation model

Vanadium–Titanium Magnetite Concentrate, Calcium–Magnesium Composite Roasting and Sulfuric Acid Leaching for Vanadium Extraction from Pellets

Investigation of Vanadium-Containing Sludge Oxidation Roasting Process for Vanadium Extraction