Abstract:Hydrogen is a potential alternative reducing agent, which can greatly reduce CO2 emission in the ironmaking process of vanadium titanomagnetite. This paper investigated the reaction process and kinetic characteristics of the hydrogen reduction of both untreated and preoxidized vanadium titanomagnetite using a thermogravimetric analyzer (TG). The effects of different preoxidation temperatures (T-oxi = 500 degrees C, T-oxi = 700 degrees C, and T-oxi = 900 degrees C) on the reduction characteristics of vanadium titanomagnetite were compared at a reduction temperature of 1000 degrees C. It was found that the reduction degree and reduction rate of low-temperature (T-oxi = 500 degrees C and T-oxi = 700 degrees C) preoxidized vanadium titanomagnetite are higher than those of high-temperature (T-oxi = 900 degrees C) preoxidized vanadium titanomagnetite. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses show that the low-temperature preoxidation process separates the Fe/Ti in vanadium titanomagnetite and forms micropores on the surface of the vanadium titanomagnetite, while the high-temperature preoxidation process allows the separated hematite and ilmenite to recombine and form pseudobrookite. The isothermal reduction experiments on untreated and preoxidized vanadium titanomagnetite were carried out, with reduction temperatures ranging from 600 to 1000 degrees C. The obtained results were subjected to kinetic analysis using conventional model-fitting and iso-conversional methods. The fitting results of different kinetic models show that the activation energies of the preoxidized vanadium titanomagnetite reduction reaction are lower than those of untreated vanadium titanomagnetite. In the entire range of the reduction reaction, the contracting area model (R-2) can best describe the reaction between hydrogen and untreated and preoxidized vanadium titanomagnetite. After the preoxidized treatment, the reduction energy barrier of vanadium titanomagnetite decreases by about 38.0%.

Direct Reduction of Solid V2O5 with Hydrogen at 600–1400 °C

Study of V<sub>2</sub>O<sub>5</sub> Direct Alloying Reductants

Extraction of Vanadium Powder by Metallothermic Reduction

Preparation of high purity vanadium

Microwave-hydrogen synergistic reduction of vanadium titano-magnetite

Isothermal reduction of V2O5 powder using H2 as oxygen carrier: Thermodynamic evaluation, reaction sequence, and kinetic analysis

Influence of Preoxidation Treatment on the Reduction Behavior and Reaction Kinetics of Vanadium Titanomagnetite by Hydrogen

Thermodynamic studies on gas-based reduction of vanadium titano-magnetite pellets

Deoxidation thermodynamics of Ti–O in hydrogen atmosphere: Preparation of TiH2 alloy powder by direct reduction of spent V2O5–WO3/TiO2 catalyst with magnesiothermic

Non-catalytic Hydrogenation of VO2 in Acid Solution

Reduction behaviors of vanadium‐titanium magnetite with H2 via a fluidized bed

1 Kinetic Studies on Gas-Based Reduction of 2 Vanadium Titano-Magnetite Pellet 3

Preparation of Oxidized Pellets of Vanadium Titanium Magnetite and Direct Reduction Behavior in Hydrogen‐Based Shaft Furnace

Kinetic Studies on Gas-Based Reduction of Vanadium Titano-Magnetite Pellet

A Method to Extract Vanadium from HIsmelt Reduction Slag: In Situ Sodium Salt Oxidation and Alkali Leaching

Recovery of Valuable Elements from Molten Vanadium Slag Through High-Temperature Reduction

Clean preparation of V2O3 by one-step molten salt electrochemical reduction of soluble NaVO3

Reduction Disintegration Behavior and Crystallographic Transformation of Vanadium-Titanium Magnetite Pellets During Hydrogen-based Reduction

Investigation of Vanadium-Containing Sludge Oxidation Roasting Process for Vanadium Extraction

Thermodynamic Study of Production of Vanadium–Nitrogen Alloy and Carbon Monoxide by Reduction and Nitriding of Vanadium Oxide

Thermodynamic study of direct reduction of high-chromium vanadium–titanium magnetite (HCVTM) based on phase equilibrium calculation model