Effect of silicate structure on thermodynamic properties of calcium silicate melts: Quantitative analysis of Raman spectra

Joo Hyun Park

DOI: https://doi.org/10.1007/s12540-013-3028-4

IF: 3.451

2013-05-01

Metals and Materials International

Abstract:The distribution of silicate anionic species (Qn units, n=0, 1, 2, 3) and the chemical speciation of oxygen in CaO-SiO2-MO (M=Mn and Mg) slags were investigated by micro-Raman spectroscopic analysis. Furthermore, the thermochemical properties were evaluated using a concentration of free oxygen and a degree of polymerization. A good linear relationship was obtained between sulfide capacity and concentration of free oxygen in the CaO-SiO2 (-MnO) melts at 1500 to 1600 °C. However, even though there was more abundant free oxygen in the CaO-SiO2-MgO system than in the CaO-SiO2 system, the sulfide capacity of the former was lower than the latter, indicating that the sulfur dissolution behavior in the silicate melts cannot be simply explained by the content of free oxygen, because the composition dependency of the stability ratio of oxygen and sulfide ions should be taken into account. The excess free energy of CaO, MgO and MnO linearly decreased as the ln (Q3/Q2) increased. The effect of the degree of polymerization on the excess free energy of mixing of MgO-containing slag was larger than that of MnO-containing slag, which was explained by the difference of the ionization potential between Mn2+ and Mg2+ ions.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to explore the influence of silicate structure on the thermodynamic properties of calcium silicate melts. Specifically, the research investigated the distribution of silicate anion species (Qn units, n = 0, 1, 2, 3) and the chemical species of free oxygen, non - bridging oxygen and bridging oxygen in CaO - SiO₂ - MO (M = Mn and Mg) slags through micro - Raman spectroscopic analysis methods. In addition, the free oxygen concentration and the degree of polymerization of silicate melts were also used to evaluate their thermochemical properties, such as sulfide capacity and partial molar excess free energy of mixing.

The main contributions of the paper are as follows:
1. A method for analyzing the structure of silicate melts was proposed, which can not only determine the configuration of discrete silicate anion units for a given composition, but also analyze the chemical species of free oxygen, non - bridging oxygen and bridging oxygen.
2. It was found that there is a good linear relationship between sulfide capacity and free oxygen concentration in CaO - SiO₂ (- MnO) melts. However, even though the free oxygen in the CaO - SiO₂ - MgO system is more abundant, its sulfide capacity is still lower than that of the CaO - SiO₂ system, indicating that the dissolution behavior of sulfur in silicate melts cannot be explained only by the free oxygen content, and the composition - dependent ratio of the stability of oxygen ions and sulfur ions also needs to be considered.
3. The research found that the excess free energies of CaO, MgO and MnO decrease linearly with the increase of ln (Q₃/Q₂). The stability of CaO is greater than that of MgO, and the latter is greater than that of MnO, which is consistent with theoretical expectations. The influence of the degree of polymerization on the excess free energy in slags with MgO content is greater than that in slags with MnO content, which can be explained by the difference in ionization potentials of Mn²⁺ and Mg²⁺ ions.

These findings are helpful for a more in - depth understanding of the relationship between the structure of silicate melts and their thermodynamic properties, and are of great significance for metallurgical processes and glass science.