Abstract:The corrosion rate of magnesium alloys is generally too high for biodegradable implant applications. This work explored combinations of anodizing and picosecond laser surface treatments to modify the corrosion response of magnesium alloy AZ31. Anodizing of the AZ31 in NaOH solutions produced porous oxide layer structures. Shallow laser treatment of these anodized surfaces, using low pulse powers, resulted mainly in oxide ablation and impaired corrosion resistance. Higher pulse power, resulting in rapid melting and resolidification into the substrate, provided an improved corrosion response. The refined grain structure produced is approximately only 5 μm deep and therefore has minimal influence on bulk mechanical properties. It is therefore a suitable process for surface modifications on small medical device structures. Controlling the initial point of degradation has been demonstrated by the use of selective laser treatment of the AZ31 surface.
What problem does this paper attempt to address?
This paper attempts to solve the problem of the excessive corrosion rate of magnesium alloys in the application of biodegradable implants. Specifically, the corrosion rate of magnesium alloy AZ31 is too high, resulting in a rapid decline in its mechanical stability in cardiovascular and orthopedic implants, which affects long - term safety and functionality. To meet this challenge, researchers explored a method combining anodization and picosecond - laser surface treatment to control and slow down the corrosion rate of magnesium alloy AZ31.
### Core issues of the paper
1. **Excessive corrosion rate of magnesium alloys**: Magnesium alloys corrode too quickly in a physiological environment, leading to a rapid decline in the mechanical properties of implants, especially in cardiovascular and orthopedic applications. This not only affects the function of the device but may also cause safety problems.
2. **Limitations of existing surface treatment methods**: Although traditional anodization treatment can provide a certain degree of anti - corrosion protection, the formed oxide layer is porous and prone to cracking during deformation, exposing the substrate and leading to rapid corrosion. Other surface treatment methods such as chemical additives or ion implantation also have problems with biocompatibility or material addition.
### Solutions
Researchers proposed a new method combining anodization and picosecond - laser surface treatment, aiming to improve the corrosion performance of magnesium alloy AZ31 in the following ways:
- **Anodization treatment**: First, an oxide layer is formed on the surface of the magnesium alloy to provide initial corrosion protection.
- **Picosecond - laser treatment**: Subsequently, the anodized surface is treated with a picosecond - laser. Through the rapid melting and resolidification process of short - pulse lasers, a denser oxide layer is formed to enhance anti - corrosion performance. It was found that appropriate laser parameters can significantly improve corrosion performance without significantly affecting the overall mechanical performance.
### Experimental results
The experimental results show that shallow - layer laser treatment (such as 55 mW and 200 mW) did not significantly improve the corrosion performance. Instead, it accelerated corrosion due to the destruction of the oxide layer. However, through high - power laser treatment (such as 3.69 W), deeper melting and resolidification can be achieved, forming a fine - grained structure with a depth of about 5 mm. This treatment method significantly improves corrosion resistance and has a relatively small impact on the overall mechanical performance.
### Conclusions
The method of combining anodization and picosecond - laser surface treatment provides an effective way to control the corrosion rate of magnesium alloy AZ31, especially suitable for small medical devices that require biodegradability. Through selective laser treatment, the location where corrosion begins can also be precisely controlled, further optimizing the degradation behavior of the device.
---