Abstract:This study presents the phase analysis, microstructural characteristics, and mechanical property evaluation of the as-cast and quenched Ti-15Mo-xFe alloys with high iron content ranging from 4 to 12 weight percent. All the four alloys were produced in a vacuum-arc melting furnace. Heat treatment in the form of solution treatment was performed in a muffle furnace at a temperature of 1100 °C, with 1-h holding time and the samples were rapidly quenched in ice-brine. X-ray diffractometer (XRD) was used to analyses the phases present in each alloy whereas the optical microscope (OM) was employed to track the microstructural evolution and percentage porosity. The mechanical properties of the alloys were evaluated using a tensile test and compression test method while the micro-Vickers hardness measurements were conducted to evaluate hardness of the alloys. The XRD patterns of as-cast showed peaks belonging to the β and α″ phases and intermetallic B2 TiFe phases. The as quenched XRD peaks illustrated β phase only and Fe·Ti·O2 phases. The as-cast OM micrographs revealed equiaxed β grains, substructures, dendritic structure, and pores forming around the grain boundaries. The quenched OM showed only β equiaxed grains with pores throughout the grain boundaries. The tensile properties such as ultimate tensile strength (UTS) and elastic modulus (E) of as-cast TMF0 were 264 MPa and 79 GPa respectively and these properties changed upon quenching to 411 MPa and 66 GPa respectively. The elastic modulus of TMF1 in as-cast condition was 74 GPa. The UTS and E of TMF1, TMF2, and TMF3 in as-cast and quenched conditions were not recorded due to the fragility of the samples that failed prior to yielding any useful data. The compressive strength in as-cast and in quenched condition decreased with an increase in Fe content. The micro-Vickers hardness in as-cast and quenched conditions showed a similar trend with hardness increasing slightly upon quenching for TMF0, TMF1, and TMF3 alloys but slightly decreased in the case of TMF2. The fracture surfaces of all the as-cast and quenched alloys were comprised of ductile and brittle fracture.

Effect of iron additions on microstructure and mechanical properties of Ni–Cr–Mo–Si hardfacing alloy

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Microstructure and Hardness Evolution During Isothermal Process at 700 °C for Fe–24Mn–0.7Si–1.0Al TWIP Steel

Structure and Oxidation Behavior of Tribaloy Alloy with Iron and Aluminum Additions

Effect of Chromium on Microstructure and Wear Resistance of Fe-Cr-C Hardfacing Alloys

Effect of Iron Content on Wear Behavior of AlCoCrFexMo0.5Ni High-Entropy Alloys

Effect of heat input on ultrahard Fe-Cr-B-C-W-Mo-Nb hardfacing

Microstructure and wear resistance of Fe-Cr-C-Mo-V-Ti-N hardfacing layers

Effect of Molybdenum on Metallurgical and Wear Properties of Fe–Cr–C Hard facing alloy

Effect of alloying elements on microstructure, wear, and corrosion behavior of Fe-based hardfacing

Effect of Ni content on microstructure and mechanical properties evolutions of 9Cr high Si heat resistant steel deposited metals

The effect of chromium additions on the mechanical properties of Ni-25Al-27.5Fe-based intermetallic compounds

Influence of Cooling Rate and Alloying by "Cr, V, and Ni" on Microstructure and High-Temperature Wear Behavior of SiMo Ductile Iron

Effect of Aluminum, Iron and Chromium Alloying on the Structure and Mechanical Properties of (Ti-Ni)-(Cu-Zr) Crystalline/Amorphous Composite Materials

Influence of the iron additive on the microstructural behavior of an aluminum-copper foundry alloy B206

Influence of intermetallic phase (TiFe) on the microstructural evolution and mechanical properties of as-cast and quenched Ti-Mo-Fe alloys

Effect of Cr Incorporation on the Mechanical Properties of HfMoTiZrCr, HfMoNbZrCr, and HfMoNbTiCr Refractory High-Entropy Alloys

Effect of Mo Content on Microstructure and Wear Resistance of Fe-Cr-C-Mo-B Hardfacing Alloys Prepared by Carbon Arc Welding

Effect of Molybdenum Contents on Microstructure and High-Temperature Wear Behavior of SiMo Ductile Iron

The Effect of Simultaneous Si and Ti/Mo Alloying on High-Temperature Strength of Fe3Al-Based Iron Aluminides