Abstract:The thermal sensitive cotton-g-PNIPAAm was prepared through free radical grafting reaction initiated by different initiators including ammonium ceric nitrate (CAN), potassium persulfate (KPS) and hydrogen peroxide/ascorbic acid (H2O2/H(2)A system). The degrees of grafting (G) achieved by different initiators could be sorted into descent order as following: G (H2O2/H(2)A) > G (KPS) > G (CAN). The other factors affecting the degree of grafting, such as the concentration of initiator, reaction time, temperature and the concentration of monomer, were studied. The results showed that the optimal conditions for grafting reaction using H2O2/H(2)A initiating system were: initiator dosage 7.5 mmol/L mole ration of H2O2 to H(2)A = 1 : 0.6), reaction time 1.5 h, monomer concentration 5% similar to 15% and the reaction temperature 25 degrees C. FTIR spectrogram of grafted cotton fiber showed characteristic absorptions of -CH3, C=O, -N-H, -C-N and -CH(CH3)(2) groups at 2967.5, 2857.4, 1623.9, 1540.3, 1457.4 cm(-1), 1385.6 and 1365.4 cm(-1) giving the evidence for the successful grafting of PNIPAAm onto cotton fiber surface. The extraneous polymer attached to fiber surface can be observed in SEM images of grafted cotton samples. DSC analysis revealed that all grafted cotton fibers had the LCST around 32 similar to 33 degrees C which was very close to the LCST of pure PNIPAAm gel (32.48 degrees C). The raising of grafting degree has little impact on LCST but increases the reversible enthalpy change (Delta H) of the cotton-g-PNIPAAm. In the falling-drop test (AATCC 79) and capillary rise test (FZ/T01071), the fabric samples of cotton-g-PNIPAAm demonstrated different water absorbing abilities at different temperatures which meant that the cotton fiber had been endowed with thermo sensibility by PNIPAAm grafting. A grafting degree between 25% similar to 45% is suitable for creating high thermo sensitivity. Other grafting degrees out of above range were not suggested. The analysis and discussion about the relationship between Delta H and swelling/shrinking time of cotton-g-PNIPAAm indicated that cotton-g-PNIPAAm reacted to temperature much quickly than pure PNIPAAm gel.

Modifying terylene/cotton blend fabric with P(AMPS/NIPA) intelligent hydrogel by graft polymerization initiated with MLTP

Thermo-responsive Poly(n-Isopropylacrylamide) Grafted Polyester Textiles with Switchable Surface Wettability

Microwave-initiated modification of polyamide 6.6 fabric surfaces for superior hydrophilic and flame retardant properties

A "grafting through" strategy for constructing Janus cotton fabric by mist polymerization

Preparation of hydrogels composites for intelligent immession fabric by coating technique

Pre-irradiation Grafting of Temperature Sensitive Hydrogel on Cotton Cellulose Fabric

Cotton fabric modification for imparting high water and oil repellency using perfluoroalkyl phosphate acrylate via γ-ray-induced grafting

Thermosensitive Behavior and Super-Antibacterial Properties of Cotton Fabrics Modified with a Sercin-NIPAAm-AgNPs Interpenetrating Polymer Network Hydrogel

Low Temperature Plasma Initiated Grafting Modification on PET Fabrics

Quaternary Ammonium Monomer Grafting Polymerization Under Ultraviolet Irradiation and Adsorption of Polypropylene Nonwovens

Radiation Grafting of Glycidyl Methacrylate and Divinylbenzene Onto Polyethylene Terephthalate Fabrics for Improving Anti-Dripping Performance

Investigation of temperature-responsive and thermo-physiological comfort of modified polyester fabric with Sericin/PNIPAAm/Ag NPs interpenetrating polymer network hydrogel

Preparation of Pnipaam Grafted Cotton and Its Thermal Sensitivity

A simple approach to design fabric with flame-retardant and pattern function

Study of Plasma-Induced Graft Polymerization of Stearyl Methacrylate on Cotton Fabric Substrates

Preparation and performance of surface modification of non-woven fabric by PVA (polyvinyl alcohol)

Improved biocompatibility and antifouling property of polypropylene non-woven fabric membrane by surface grafting zwitterionic polymer

Anti-dripping PET Fabrics Prepared by Two Steps Radiation-induced Grafting

Fabrication of Fast Responsive, Thermosensitive Poly(n-Isopropylacrylamide) Hydrogels by Using Diethyl Ether As Precipitation Agent.

The Method of Introduced Amino Group for Preparation of Thermo-Responsive Textiles

Fabrication and Property Optimization of Electrostatic Spinning PVDF/PDMS Waterproof and Moisture Permeable Membrane