Abstract:Failure response of the modern high strength steel grades shows a diverse pattern compared to the conventional highly ductile steels. In automotive sheet forming applications of the high strength steels, fracture could be observed prior to necking or the post necking deformation is very limited. The differences in the underlying damage mechanisms contribute to the different ways of damage development and the interaction of damage with plastic localization and strain hardening creates various failure patterns. Therefore, it is critical to clearly identify the phase for damage initiation and understand the relation between plastic localization, damage and fracture, as these patterns significantly influence the safety assessment in the forming process of steels. Inverse modelling approaches are being used to bridge the gap between experiments and numerical simulations. However, this technique shows significant discrepancies when strain heterogeneity is experienced, especially since the determination of the material parameters is based on comparison on a global scale with force and elongation measurements. An iterative finite element model update (FEMU) procedure integrated with optical full field measurement technique was executed which extended the possibilities to identify the material ductile damage and fracture behavior on a local level with significantly higher accuracy. To identify the material plastic and damage behavior of the automotive dual phase steel (DP-K1000) under study, experiments are conducted on dog-bone, notched tensile, central hole and shear specimens at various strain rates. Full field deformation data was obtained by digital image correlation (DIC). A vigorous and general framework for the inverse identification of the strain hardening behavior up to fracture of the automotive high strength steel was studied. A hybrid damage mechanics model (extended Modified Bai-Wierzbicki) that combines a phenomenological criterion for damage initiation related to the microstructure degradation of materials and a continuum damage mechanics based damage evolution law for progressive damage accumulation till final fracture is employed using a VUMAT in the finite element (FE) scheme. To exclude the convergence (plastic instability) problems, a displacement driven finite element simulation was used while minimizing the discrepancy between the experimental and numerical surface strain fields and force values. A visual mapping procedure was adopted to realize identical reference frames and therefore identical peripheries for the specimen in DIC and FE model. This mapping includes a transformation and interpolation function from FE results to the DIC datum points. Successful identification of the material parameters was achieved based on a combined Gauss-Newton and Levenberg-Marquardt algorithm which require the evaluation of the gradient of the objective function to update the unknown parameters in an appropriate direction. The optimization problem of the inverse modelling in the current work was described by a cost function based on the least square norm of the differences of the surface strain fields. Overall cost function formulation is not dependent on the experimental or finite element meshes and includes rigid body motions. The residual was minimized at once for all the displacements by Gauss-Newton scheme in space-time, which is defined by spatial domain and temporal domain. The optimization of the constitutive parameters was directly achieved by minimizing this image residual in an iterative manner. The adopted methodology helped in determining macroscopic crack initiation instant and location from experiments. Local variables such as equivalent plastic strain, stress triaxiality and Lode angle parameter were evaluated from the critical element for the determination of the damage initiation locus which was then fitted by a non-linear least squares method with a trust-region algorithm in Matlab. The identified damage initiation locus and plastic localization phenomena served as an evaluation criteria for the formability of the dual phase automotive steel.

Ductile damage measurement and necking analysis of metal sheets based on digital image correlation and direct current potential drop methods

Approach to investigate pre-nucleation fatigue damage of cyclically loaded metals using Vickers microhardness tests

Depth-Sensing Indentation-Based Studies of Surface Mechanical Behavior and Fatigue Damage Evolution of an Austenitic Stainless Steel Subjected to Cyclic Straining

An approach to investigating evolution of fatigue damage on surface of structural steel based on microhardness

DIC/DSI Based Studies on the Local Mechanical Behaviors of HR3C/T92 Dissimilar Welded Joint During Plastic Deformation

A New Approach for Studying Fatigue Damage

Experimental techniques for ductile damage characterisation

Parametrisation of Uniform Deformation in Ductile Metals Using Digital Image Correlation Technology

Practical Applicability and Limitations of the Elastic Modulus Degradation Technique for Damage Measurements in Ductile Metals

A rate-dependent damage mechanics model for predicting plasticity and ductile fracture behavior of sheet metals at high strain rates

Enhanced CDM model accounting of stress triaxiality and Lode angle for ductile damage prediction in metal forming

Experimental analysis of strain path dependent ductile damage mechanics and forming limits

Investigation of various necking criteria for sheet metal formability analysis using digital image strain data

Application of 3D digital image correlation for the measurement of the tensile mechanical properties of high-strength steel

Fracture of dual phase steel sheets under uniaxial tension (I): experimental study with dic techniques

Stress Triaxiality in Anisotropic Metal Sheets—Definition and Experimental Acquisition for Numerical Damage Prediction

Size Effect on the Post-Necking Behaviour of Dual-Phase 800 Steel: Modelling and Experiment

Correlation Between Acoustic Emission Detection and Microstructural Characterization for Damage Evolution

Fracture prediction for metal sheet deformation under different stress states with uncoupled ductile fracture criteria

A direct analytical methodology for the assessment of ductile fracture in metals based on multiaxial tests

Revealing plastic localization and ductile damage initiation features with integrated DIC and FEM