Abstract:Steels are abundantly used in many areas because of their good formability and low price. Steels suffer from corrosion in aqueous environments with chloride ions. Corrosion of steels is also a serious problem for long-term usage of steel structures such as bridges and buildings. There are many studies focused on chloride ions. There are reports that metal cations have a tendency to inhibit the corrosion of steels in a chloride aqueous environment by forming a layer on the steel. The other important factor for corrosion of steels in an aqueous environment is temperature. The corrosion rate of metal in cold regions is expected to slow because of low temperature. A recent study on atmospheric exposure tests carried out in different places in Hokkaido, it has elucidated that the corrosion rate in the cold region is the same as in the warm region. However, it is not fully elucidated that temperature, especially below freezing point, and metal cations on corrosion behavior and distribution of active dissolution site. The purpose of this study is to investigate the influence of temperature and metal cations on thecorrosion behavior of steels. Steel sheets of 15 x 20 mm and 20 x 20 mm were used as specimens. Three solutions of 0.1 mM ZnCl 2 , 0.5 mM ZnCl 2 and 1.0 mM ZnCl 2 were used for examination of the effect of metal cations, and 20 mass % NaCl solution was used for examination of effect of temperature. After the tests, the morphology of specimens was examined by optical microscope and scanning electron microscope. After the wet/dry corrosion tests used 10 mL solutions droplets, corrosion products were formed on the specimens. The corrosion processes under NaCl and MgCl 2 were similar. Yellow corrosion products were firstly observed in the solution during the wet period. In the case of under ZnCl 2 , after the formation of oxide layer on the specimens the corrosion proceeded in localized areas. The color of almost half area of the exposed surface was light, which might indicate less corrosion occurred in the area. The initial corrosion stage of steel preferred to form a brown area in the center of the droplet. There are no similar corrosion products thatcan be observed in comparison to the samples under MgCl 2 and NaCl solutions. A lot of corrosion products and localized corroded areas were formed on specimens after being immersed at 273 K, while less corrosion products and homogenously corroded surface were observed on specimens after being immersed at 293K. The results indicated that corrosion morphology and preferentially corroded area were changed with the kind of metal cation and temperature.

Corrosion Behaviour of T92 Steel in NaCl Solution

Differences of the High‐temperature Corrosion of Ferrite Steel T92 Caused by Applied Stresses and NaCl–Na2SO4 Molten Salts

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

Corrosion Behaviors of TWIP Steels in NaCl Solution

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Effects of External Stress on High-Temperature Corrosion Behavior of T92 Ferrite Steel with Na2SO4-K2SO4 Molten Salts

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

EFFECT OF CHLORIDE ION ON CORROSION BEHAVIOR OF N80 STEEL IN CO2 SOLUTIONS

Effects of Imposed Stresses on High Temperature Corrosion Behaviour of T91

CORROSION BEHAVIOR OF STAINLESS STEEL 304 AS WATER SUPPLY MATERIAL IN WATER CONTAINING CHLORIDE

Corrosion Behavior of 9 % Ni Steel for LNG Storage Tanks in 3.5 Wt. % NaCl Solution

Corrosion Processes of Weathering Steels in 2.0% Nacl Neutral Solutions

Corrosion Behavior of Q235 Steel in Atmospheres Containing SO2 and NaCl

Pitting corrosion of low alloy steel in environment of strongly acidic solution containing chloride ion

Corrosion Behavior of 20G Steel in Saline (na2so4) Circumstances at High Temperature/Pressure

Influence of Metal Cation and Temperature on Localized Corrosion Behavior of Steels in Aqueous Environments

Corrosion Behaviors of Fe-22Cr-16Mn-0.55N High-Nitrogen Austenitic Stainless Steel in 3.5% NaCl Solution

Corrosion behavior and mechanism of 316 stainless steel in NaCl-KCl-ZnCl2 molten salts at high temperature

Corrosion Mechanism of Nanocrystalline Zinc Coating on Steel Sheet Used for Automobile in NaCl Solution

Electrochemical Study on Corrosion Process Characteristics of the High-Strength Low-Alloy Steels in NaHSO 3 Solution

ROLE OF NaCl IN THE ATMOSPHERIC CORROSION OF A3 STEEL