Abstract:Nanosized titanium dioxide (TiO2) powders were prepared by an aqueous sol–gel method using an inorganic titanium precursor, titanium oxysulfate (TiOSO4). The synthesized powders were characterized by XRD, N2 sorption analysis, SEM, TEM, FTIR and UV-vis DRS spectroscopy. The important synthesis parameters such as precursor concentration, precipitating pH value, peptization temperature, aging time and temperature, heating rate and time and calcination temperature were systematically investigated for their effect on the physicochemical and photocatalytic properties of TiO2. XRD analysis revealed that powders prepared at precipitating pH value ranges from 5 to 9, calcined at 300–600 °C were composed of anatase and brookite. UV-vis DRS analysis showed that the variation in band gap for composite mixture is related to the fraction of brookite and rutile phase. Using low precursor concentration (0.1 and 0.2 M) the final material was composed of anatase–brookite composite mixture, in contrast, at high precursor concentration (0.4 M), pure anatase TiO2 was formed. An increase in aging time beyond 24 h favors the phase transformation of brookite into anatase and increase in peptization temperature from 40 to 70 °C shows a great influence on crystal structure, leading to enhanced crystallization rate with the formation of pure anatase phase. The synthesized powders activity was tested in the degradation of an aqueous solution of 4-chlorophenol (4-CP) under UV light. The TiO2 powder prepared at pH 6 and calcined at 300 °C showed the highest activity, which is attributed to powder composite nature (anatase–brookite; 81–19 wt.%), relative high specific area (157.0 m2 g−1), high crystallinity and degree of hydroxyl groups and moderate band gap. In addition, in terms of reusability, recyclability and chemical stability, the developed photocatalyst showed very encouraging results.

Sol–gel synthesis of TiO2 from TiOSO4: characterization and UV photocatalytic activity for the degradation of 4-chlorophenol

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Preparation of Nanocrystalline TiO2 Powders for Photocatalytic Oxidation of Phenol

Photocatalytic Degradation of 2,4-Dichlorophenol by TiO2 Intercalated Talc Nanocomposite

Hydrothermal synthesis of TiO2 hollow microspheres for the photocatalytic degradation of 4-chloronitrobenzene

Preparation of Nano-Tio2 Photocatalysts and Their Decomposition Activity in Phenol-Contaminated Water

Nanocrystalline anatase TiO2 photocatalysts prepared via a facile low temperature nonhydrolytic sol–gel reaction of TiCl4 and benzyl alcohol

Photocatalytic degradation of organic contaminants by TiO 2/sepiolite composites prepared at low temperature

Facile Growth and Characterization of TiO2 Nanoparticles for Photocatalytic Degradation of 2,3-Dichlorophenol: Experimental Optimization and Comparison with Commercial TiO2.

Cement Bonded Sol-Gel TiO2 Powder Photocatalysis for Phenol Removal

Photocatalytic activity of TiO 2 nanorods, nanowires and nanoflowers filled with TiO 2 nanoparticles

Phenol degradation by TiO2 photocatalytic technology

The Preparation and Characterization of N-F-Sm-TiO2 Sol and Its Photocatalytic Degradation for 4-Chlorophenol

Preparation of Anatase F-TiO2 and Its Performance for the Photodegradation of 4-Chlorophenol

PHOTOCATALYTIC DEGRADATION OF PHENOL AND CHLORINATED PHENOLS USING NANOMETER TiO2 THIN FILMS

Tailored preparation of titania with controllable phases of anatase and brookite by an alkalescent hydrothermal route

Hydrothermal Synthesis of Graphene Grafted Titania/titanate Nanosheets for Photocatalytic Degradation of 4-Chlorophenol: Solar-light-driven Photocatalytic Activity and Computational Chemistry Analysis

Preparation of bismuth oxide/titania composite particles and their photocatalytic activity to degradation of 4-chlorophenol

Application of Fe~(3+)-doped Nano-TiO_2 by Sol-gel Hydrothermal Synthesis

Efficient Sonochemical Degradation of 4-Chlorophenol Catalyzed by Titanium Dioxide Hydrate