Abstract:Bimetallic CoCu model catalysts were investigated for the synthesis of higher alcohols using catalytic CO hydrogenation according to the Fischer–Tropsch technology. Emphasis was placed on revealing the influence of the activation conditions. Accordingly, catalyst precursors were activated in argon, hydrogen, syngas (CO/H2), and CO under atmospheric conditions and at elevated temperatures (370 °C). All catalyst precursors were prepared via oxalate coprecipitation in the absence of a classic support. Alcohol selectivities between 30 and ∼40% (up to ∼50% for the sum of alcohols and alkenes) were obtained with an Anderson–Schulz–Flory (ASF) chain lengthening probability maximizing the slate up to C6. Detailed catalysis and characterization studies were performed using a Co2Cu1 catalyst composition. The catalytic performances of the H2- and syngas-activated Co2Cu1 catalyst were similar. While the CO-activated catalyst shows significantly higher catalytic activity and ASF chain lengthening probability, the alcohol selectivities are lower than those of H2- or syngas-activated ones. All catalysts required time on stream for several hours to achieve steady-state catalytic performance. Co2Cu1 catalysts were characterized by temperature-programmed decomposition (TPDec), in situ N2 physisorption (Brunauer–Emmett–Teller), transmission electron microscopy (TEM), and in situ X-ray photoelectron spectroscopy (XPS). The data indicate major restructuring occurs during activation. An “onion-like” graphitic carbon shell was observed via TEM for the CO-activated Co2Cu1 catalyst, which probably originated mainly from the Boudouard reaction (2CO + [ ]ad → Cad + CO2). This interpretation is in accordance with the TPDec profiles and XPS results. The latter also indicates that syngas and CO activation lead to higher than nominal Co/Cu surface ratios. The surface segregation of Co in the presence of CO atmospheres is interpreted on the basis of Co@Cu core–shell structured particles.

Elucidating the Copper–Hägg Iron Carbide Synergistic Interactions for Selective CO Hydrogenation to Higher Alcohols

Theoretical Investigation on the CO2 Hydrogenation to Methanol Mechanism at Electron-Rich Active Interface over Cu/Ga-Ti-Al-O Catalyst

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

Mechanistic Insight into Hydrocarbon Synthesis via CO2 Hydrogenation on χ-Fe5C2 Catalysts

Synthesis of mixed higher alcohols over Fe promoted Cu/ZrO2 catalysts by CO hydrogenation

Theoretical investigation of the selectivity of alcohols and aldehydes on Co-based catalysts in syngas conversion

Higher Alcohols through CO Hydrogenation over CoCu Catalysts: Influence of Precursor Activation

Insight into the structural sensitivity of CuZnAl catalysts for CO hydrogenation to alcohols

The Selectivity and Activity of Catalyst for Co Hydrogenation to Methanol and Hydrocarbon: A Comparative Study on Cu, Co and Ni Surfaces

Tuning the selectivity of CO2 hydrogenation to alcohols by crystal structure engineering

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

Isolated dual-active Fe-Co sites efficiently promote CO 2 hydrogenation upgrading

Moderate Surface Segregation Promotes Selective Ethanol Production in CO2 Hydrogenation Reaction over CoCu Catalysts

Syngas conversion to higher alcohols via wood-framed Cu/Co-carbon catalyst

Edge-rich molybdenum disulfide tailors carbon-chain growth for selective hydrogenation of carbon monoxide to higher alcohols

Revealing and Regulating the Complex Reaction Mechanism of CO 2 Hydrogenation to Higher Alcohols on Multifunctional Tandem Catalysts

Rh-Decorated Cu Alloy Catalyst for Improved C-2 Oxygenate Formation from Syngas

Co Hydrogenation to Ethanol and Higher Alcohols Over Ultrathin Cucoal Nanosheets Derived from Ldh Precursor