Research on flow behaviors of the constituent grains in ferrite–martensite dual phase steels based on nanoindentation measurements

Rui-bin Gou,Wen-jiao Dan,Wei-gang Zhang,Min Yu

DOI: https://doi.org/10.1088/2053-1591/aa7d95

IF: 2.025

2017-07-27

Materials Research Express

Abstract:To investigate the flow properties of constituent grains in ferrite–martensite dual phase steel, both the flow curve of individual grain and the flow behavior difference among different grains were investigated both using a classical dislocation-based model and nanoindentation technique. In the analysis of grain features, grain size, grain shape and martensite proximity around ferrite grain were parameterized by the diameter of area equivalent circular of the grain d, the grain shape coefficient λ and the martensite proximity coefficient p, respectively. Three grain features influenced significantly on the grain initial strength which increases when the grain size d decreases and when grain shape and martensite proximity coefficients enlarge. In describing the flow behavior of single grain, both single-parameter and multi-parameter empirical formulas of grain initial strength were proposed by defining three grain features as the evaluation parameters. It was found that the martensite proximity is an important determinant of ferrite initial strength, while the influence of grain size is minimal. The influence of individual grain was investigated using an improved flow model of overall stress on the overall flow curve of the steel. It was found that the predicted overall flow curve was in good agreement with the experimental one when the flow behaviors of all the constituent grains in the evaluated region were fully considered.

materials science, multidisciplinary