Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Synthesis of thermotropic polybenzoxazole using 3-amino-4-hydroxybenzoic acid

Synthesis and Properties of a Novel Bio-based Benzoxazine

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Novel Thermally Stable and Organosoluble Aromatic Polyamides with Main Chain Phenyl-1,3,5-Triazine Moieties

Synthesis and Thermal Properties of Polybenzoxazole from Soluble Precursor with Hydroxy-Substituted Polyenaminonitrile

Computer-aided design of thermosetting benzoxazoles containing bis-endoalkynyl groups: Low melting points and high thermal stability

A Bio-Based Polybenzoxazine Derived from Diphenolic Acid with Intrinsic Flame Retardancy, High Glass Transition Temperature and Dielectric Properties.

Tailoring thermosetting benzoxazoles for optimal performance: Balancing thermal stability, dielectric properties, and processability

Synthesis and Characterization of Α,ω-Bis(2,6-dimethylphenol)-poly(2,6-dimethyl-1,4-phenylene Oxide) Oligomers in Water and the End-Group Modification

Synthesis, ring-opening polymerization, and properties of benzoxazines based on o- and p-hydroxybenzyl alcohols

Branched Fluorine/Adamantane Interfacial Compatibilizer for PBO Fibers/Cyanate Ester Wave-Transparent Laminated Composites

Synthesis, polymerization and thermal properties of bio‐based benzoxazine resins containing imide or amide functionality

Synthesis, characterization, and thermal properties of benzoxazine monomers containing allyl groups

Synthesis of Branched Benzoxazine Monomers with High Molecular Mass, Wide Processing Window, and Properties of Corresponding Polybenzoxazines

Syntheses of Organic Solvent-Soluble Polybenzimidazole Derivatives with a Guanidinoid Structure

Synthesis of triphenol‐diamine‐type hyperbranched benzoxazine and improvement of thermal properties and toughness of typical benzoxazines

Synthesis of phosphaphenanthrene-functional monobenzoxazine for enhancing thermal properties of polybenzoxazine thermosets

Hybrid Polymer Membrane Functionalized PBO Fibers/Cyanate Esters Wave-Transparent Laminated Composites

De novo biosynthesis of 2-hydroxyterephthalic acid, the monomer for high-performance hydroxyl modified PBO fiber, by enzymatic Kolbe–Schmitt reaction with CO2 fixation