Experimental study on the hole machining process of a newly developed AFRP/Al/AFRP co-cured material: A comparative analysis of milling and drilling
Wentian Shi,Tong Ma,Jie Li,Xiaoqing Zhang,Lin Wang,Yilin Yang,Zhenyang Wen,Jianing Li
DOI: https://doi.org/10.1016/j.jmapro.2024.10.019
IF: 5.684
2024-10-15
Journal of Manufacturing Processes
Abstract:In this paper, the milling and drilling processing methods were used to make holes in AFRP/Al/AFRP laminated materials, the study investigated the impact of parameters of machining for hole quality and surface defects. It analyzed the mechanism based on cutting heat and cutting force. On this basis, a comparison with the hole-making experiment of AFRP was also conducted to reveal the differences in the fiber breakage mode and surface creation mechanism of the two materials under different machining methods. The test results indicate that the hole milling process exhibits higher milling of quality and the cutting temperature is lower, which is about 90.539% of the drilling process. In addition, the axial force during hole-making was lower, about 52.383% of that of drilling. Compared with single AFRP material cutting, the system stiffness of co-cured material was significantly improved. Still, the cutting temperature was higher ( 25.266% increase), in the hole-making the thrust force was higher ( 59.383% increase), and the surface of that bore wall was susceptible to mechanical damage, resulting in poor overall machining quality. The results of the study shows that in the hole milling process, the upward stripping effect is weak, and the material mostly consists of short burrs that primarily cause shear fracture and form the edge of the hole. Under drilling conditions, the downward stamping effect is stronger, the fibers have a partial tensile fracture, and the orifice edge is dominated by long fibers. In conclusion, this study will further deepen the cutting and processing mechanism of the laminated materials. Simultaneously, it will enhance the scope of use and application prospects of AFRP.
engineering, manufacturing