I. A. Stenina,R. R. Shaydullin,T. L. Kulova,A. M. Skundin,A. B. Yaroslavtsev
Abstract:The Li4Ti5O12/polyaniline and Li4Ti5O12/С/polyaniline composite materials with different lithium titanate/aniline ratio of 8:1, 4:1, 2:1, 1:1, 1:2, and 1:4 were synthesized by in situ polyaniline (PANI) polymerization. The materials were characterized by high-resolution TEM, X-ray powder diffraction, IR spectroscopy, and TGA. It was shown that polyaniline is uniformly distributed over the surface of Li4Ti5O12 or Li4Ti5O12/С composite. For the sample with the minimum polyaniline content (Li4Ti5O12/С/PANI (8:1)), the PANI layer thickness is 2–3 nm and contains polyaniline in the most conductive (emeraldine) form. The lithium titanate modification with polyaniline results in sharp increase in the electronic conductivity of materials from ~ 10−11 Ohm-1 cm−1 for Li4Ti5O12 to 10−4 Ohm-1 cm−1 for Li4Ti5O12/C/PANI. With increasing polyaniline content, the electrochemical capacity decreases for all samples, including carbon-coated and uncoated ones. The highest discharge capacity at current density < 800 mA g−1 is attained for the Li4Ti5O12/С/PANI (8:1) composite.
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the electrical conductivity and electrochemical performance of lithium titanate oxide (Li₄Ti₅O₁₂) as the anode material of lithium - ion batteries. Specifically, Li₄Ti₅O₁₂ is modified by using polyaniline (PANI) and carbon coating to overcome its inherent problems of low electron and ion conductivity, thereby enhancing its cycling stability and electrochemical capacity at high current densities.
### Main research contents:
1. **Material synthesis**:
- Li₄Ti₅O₁₂/polyaniline (PANI) and Li₄Ti₅O₁₂/carbon/polyaniline composites with different Li₄Ti₅O₁₂/aniline ratios (8:1, 4:1, 2:1, 1:1, 1:2, and 1:4) were synthesized by in - situ polymerization method.
- The introduction of the carbon coating was achieved by adding sucrose to the Li₄Ti₅O₁₂ precursor and then calcining at a high temperature in an argon atmosphere.
2. **Material characterization**:
- The materials were characterized in detail using high - resolution transmission electron microscopy (HR - TEM), X - ray powder diffraction (XRD), infrared spectroscopy (IR) and thermogravimetric analysis (TGA).
- The results showed that polyaniline was evenly distributed on the surface of Li₄Ti₅O₁₂ or Li₄Ti₅O₁₂/carbon composites, and in the sample with the lowest polyaniline content (Li₄Ti₅O₁₂/carbon/PANI (8:1)), the PANI layer thickness was 2 - 3 nm and was in the most conductive emeraldine form.
3. **Conductivity test**:
- The conductivity of the Li₄Ti₅O₁₂/carbon/PANI composite modified by polyaniline was significantly improved, increasing from about 10⁻¹¹ Ω⁻¹·cm⁻¹ of pure Li₄Ti₅O₁₂ to 10⁻⁴ Ω⁻¹·cm⁻¹.
- As the polyaniline content increased, the conductivity continued to increase, but the electrochemical capacity decreased.
4. **Electrochemical performance test**:
- The charge - discharge performance of the composites was tested at different current densities.
- The results showed that when the current density was lower than 800 mA g⁻¹, the Li₄Ti₅O₁₂/carbon/PANI (8:1) composite exhibited the highest discharge capacity.
- At high current densities, due to the low conductivity of polyaniline becoming an obstacle to rapid lithium intercalation, its electrochemical performance was not as good as that of the unmodified Li₄Ti₅O₁₂.
### Conclusions:
- Through carbon coating and polyaniline modification, the conductivity of Li₄Ti₅O₁₂ was significantly improved, from about 10⁻¹¹ Ω⁻¹·cm⁻¹ to 10⁻⁴ Ω⁻¹·cm⁻¹.
- Polyaniline was evenly distributed on the surface of Li₄Ti₅O₁₂, and in the sample with the lowest polyaniline content, the PANI layer thickness was 2 - 3 nm and was in the most conductive emeraldine form.
- As the polyaniline content increased, the electrochemical capacity of all composites decreased.
- When the current density was lower than 800 mA g⁻¹, the Li₄Ti₅O₁₂/carbon/PANI (8:1) composite exhibited the best electrochemical performance, but at high current densities, the low conductivity of polyaniline became a limiting factor.
### Formula representation:
- Conductivity unit: \(\text{Ω}^{-1}\cdot\text{cm}^{-1}\)
- Discharge capacity unit: \(\text{mAh g}^{-1}\)
- Cycle stability calculation formula:
\[
n=\frac{Q_1 - Q_{50}}{50}\times\frac{100\%}{Q_1}
\]
where \(Q_1\) and \(Q_{50}\) are the discharge capacities of the 1st and 50th cycles respectively.