Abstract:Metal-organic framework (MOF) materials are promising precursors to transition into metal-nitrogen-carbon (M-N-C) catalysts with high catalytic performance. Pyrolysis is one of the most common ways to convert MOFs into electrically conductive MOF-derived M-N-C catalysts. General interests in using MOFs as precursors derive from changing the MOFs' porous structure into the carbonaceous frame. However, this favorable structure is not always maintained, with the reason unidentified since pyrolysis is currently still more of an empirical process. Understanding the pyrolysis processes leading to the transformation of MOFs into M-N-C catalysts is essential to broaden the development of MOF-derived catalysts. We report here complete chemical and morphological evolution and transformation of two commercial MOFs with the same sodalite topology, the ZIF-8 and ZIF-67, via series of in situ and ex situ techniques. The results reveal that the structure of the ZIF-67 collapses after the pyrolysis due to the graphitization of the carbon. Graphitization is catalyzed by the metallic cobalt particles formed when the temperature rose above 460 °C. The ZIF-8 was found to be a promising precursor material since most of the metal evaporates at the early stages and does not aggregate to form metal particles. However, the insufficient metal-N active sites and intrinsic low electrocatalysis availability of Zn limit the performance of the final catalyst. To maintain the porous structure of MOFs it is important to control the metal species and prevent them from agglomeration. Direct utilization of high-concentration MOFs as pyrolysis precursors is not recommended without rational design to inhibit agglomeration and graphitization that are undesirable for catalyst activity.

ZIF-derived metal/N-doped porous carbon nanocomposites: efficient catalysts for organic transformations

Metal/Porous Carbon Composites for Heterogeneous Catalysis: Old Catalysts with Improved Performance Promoted by N-Doping

Metal Embedded Porous Carbon for Efficient CO2 Cycloaddition under Mild Conditions

Nitrogen-Rich Precursors Assisted Synthesis of Metal-Organic Framework-Derived Nanostructures As Bifunctional Catalysts for Electrochemical Sensing and Oxygen Reduction Reaction

Structural Design of Metal Catalysts Based on ZIFs: from Nanoscale to Atomic Level

From Bimetallic Metal‐Organic Framework to Porous Carbon: High Surface Area and Multicomponent Active Dopants for Excellent Electrocatalysis

Metal‐Organic Frameworks: from Bimetallic Metal‐Organic Framework to Porous Carbon: High Surface Area and Multicomponent Active Dopants for Excellent Electrocatalysis (adv. Mater. 34/2015)

Conversion of a Metal-Organic Framework to N-doped Porous Carbon Incorporating Co and CoO Nanoparticles: Direct Oxidation of Alcohols to Esters.

Anchoring Metal-Nitrogen Sites on Porous Carbon Polyhedra with Highly Accessible Multichannels for Efficient Oxygen Reduction

Nanowire-Directed Templating Synthesis of Metal-Organic Framework Nanofibers and Their Derived Porous Doped Carbon Nanofibers for Enhanced Electrocatalysis

Confined pyrolysis transformation of ZIF-8 to hierarchically ordered porous Zn-N-C nanoreactor for efficient CO2 photoconversion under mild conditions

Metal-organic-frameworks derived cobalt embedded in various carbon structures as bifunctional electrocatalysts for oxygen reduction and evolution reactions

N,S co-doped hierarchically porous carbon materials for efficient metal-free catalysis

Three-dimensional MOF-derived Co and N co-doped porous carbon bifunctional catalyst for the Zn–air battery

Development of Mof-Derived Carbon-Based Nanomaterials for Efficient Catalysis

Atomically Dispersed Fe/N-Doped Hierarchical Carbon Architectures Derived from a Metal–Organic Framework Composite for Extremely Efficient Electrocatalysis

Metal–organic Framework-Derived Porous Materials for Catalysis

Catalysts by pyrolysis: Transforming metal-organic frameworks (MOFs) precursors into metal-nitrogen-carbon (M-N-C) materials

Nanostructural engineering of metal-organic frameworks: Construction strategies and catalytic applications

Zif-Derived Porous Carbon Supported Pd Nanoparticles Within Mesoporous Silica Shells: Sintering- and Leaching-Resistant Core-Shell Nanocatalysts

Metal–Organic‐Framework‐Derived Hollow N‐Doped Porous Carbon with Ultrahigh Concentrations of Single Zn Atoms for Efficient Carbon Dioxide Conversion