Abstract:To address the severe corrosion problems faced by steel, a natural corrosion inhibitor derived from Camellia Oleifera shell extract (COSE) was developed. The effectiveness of COSE as well as its synergistic mixture of COSE/ KI in inhibiting the corrosion of steel in H 2 SO 4 was investigated using weightlessness and electrochemical techniques. The results show that the maximum inhibition efficiency of individual COSE is 77.28 % at 20 degrees C, and is increased to 93.08 % for the mixture of COSE/KI. The adsorption of COSE, KI and COSE/KI on steel surface conform to Langmuir adsorption isotherm. COSE/KI has a stronger adsorption than either COSE or KI. Electrochemical analysis indicates that COSE/KI is a hybrid inhibitor primarily focusing on the cathodic inhibition. Mixing COSE with KI shows considerably larger charge transfer resistance and smaller double -layer capacitance than individual COSE and KI. Characterization tests such as metallurgical microscopy, SEM, AFM and contact angle confirm that the addition of COSE/KI could reduce the roughness of steel surface, while increase the hydrophobicity, then effectively alleviate the corrosion on the steel surface. XPS analyses demonstrated that the corrosion inhibition layer on the steel surface was induced by the adsorption of the polar groups in COSE. The components responsible for COSE ' s effectiveness were thoroughly examined using FTIR and liquid chromatography -mass spectrometry (LC -MS), which identified the presence of compounds such as flavonoids and phenylpropanoids. The synergistic effect of the active ingredients (rutin, quercetin, tea saponin, tea polyphenols, et al.) with KI was also confirmed. Finally, theoretical calculations were conducted to analyze properties of rutin, quercetin and tea polyphenols on the iron layer. The results show all these molecules exhibit efficient inhibition, with quercetin showing better inhibitive ability by parallel adsorption.

Kapok leaves extract and synergistic iodide as novel effective corrosion inhibitors for Q235 carbon steel in H2SO4 medium

Evaluating the Synergistic Effect of Maple Leaves Extract and Iodide Ions on Corrosion Inhibition of Q235 Steel in H2SO4 Solution

Synergistic Effect of KI on Corrosion Inhibition of Carbon Steel by Styphnolobium Japonicum (L.) Schott in H2SO4 Solution

Synergistic Mixture of Camellia Oleifera Shell Extract and KI As an Eco-Friendly and Highly Efficient Composite Inhibitor for Steel Corrosion in H2SO4 Media

The synergistic inhibition effects of oleic imidazoline quaternary ammonium salt and sulfonate on Q235 steel corrosion in HCl media

Synergistic Inhibition Effects of Bamboo Leaf Extract/Major Components and Iodide Ion on the Corrosion of Steel in H3po4 Solution

Investigating the Synergistic Effect of Iodide Ion and Michelia Alba Leaf Extract on Carbon Steel in 0.5M H2SO4

Capsella Bursa-Pastoris Extract As an Eco-Friendly Inhibitor on the Corrosion of Q235 Carbon Steels in 1mol·l−1 Hydrochloric Acid

Synergistic mixture of Eupatorium adenophora spreng leaves extract and KI as a novel green inhibitor for steel corrosion in 5.0 M H<sub>3</sub>PO<sub>4</sub>

Tailoring poly(2-ethyl-2-oxazoline) towards effective mitigation of chloride-induced dissolution of S235JR steel: The synergistic contributions of potassium iodide and myristyl trimethylammonium bromide

A New Imidazole Derivative for Corrosion Inhibition of Q235 Carbon Steel in an Acid Environment

Synergistic Inhibition Effect Between Capsella Bursa-Pastoris Extracts and Iodide Ions for Q235 Mild Steel in 1 M HCl Solution

Locust Bean Gum As a Green and Novel Corrosion Inhibitor for Q235 Steel in 0.5 M H2SO4 Medium

Corrosion Inhibition Effect of a New Quinoline Derivative on Q235 Steel in H2SO4 Solution

Corrosion Inhibition of Q235 Mild Steel in 0.5 M H2so4 Solution by Phytic Acid and Synergistic Iodide Additives

Study on Synergistic Corrosion Inhibition Effect between Calcium Lignosulfonate (CLS) and Inorganic Inhibitors on Q235 Carbon Steel in Alkaline Environment with Cl−

Experimental and Theoretical Study on the Synergistic Inhibition Effect of Pyridine Derivatives and Sulfur-Containing Compounds on the Corrosion of Carbon Steel in CO₂-Saturated 3.5 wt.% NaCl Solution

Preparation of Isoetes sinensis Extract as a Green Corrosion Inhibitor for Q235 Carbon Steel in Hydrochloric Acid

Synergistic Mixture of Eupatorium Adenophora Spreng Stems Extract/ki As an Efficient Inhibitor for the Corrosion of Steel in H2SO4

Experimental and Theoretical Study on the Synergistic Inhibition Effect of Pyridine Derivatives and Sulfur-Containing Compounds on the Corrosion of Carbon Steel in CO2-Saturated 3.5 wt.% NaCl Solution

Corrosion Inhibition by Amino Acid Functionalized Chitosan Derivative at Q235 Steel/ H2SO4 Solution Interface: Experimental and Surface Investigations