Investigation of Glass Fiber Reinforcement Effect on the CBR Strength of Cohesive Soil

Suchit Kumar Patel,Baleshwar Singh

DOI: https://doi.org/10.1007/978-981-13-0559-7_8

2018-09-02

Abstract:An experimental study was carried out to investigate the application suitability of randomly distributed glass fiber-reinforced cohesive soil as subgrade material. Glass fiber of 20 mm length with varying fiber contents (fc = 0.25, 0.5, 0.75 and 1% by dry weight of soil) was used as reinforcement. The effects of fiber content variation on compaction parameters of soil, and the effect of fiber content and soaking time variation on CBR strength were investigated. The soaking time was varied from 4 to 40 days. The CBR and secant modulus were calculated at different penetration depths ranging from 2.54 to 12.7 mm. Test results have shown that the glass fiber content has insignificant effect on the OMC and MDD of the soil. The CBR strength is found to increase with penetration depth up to 7.62 mm penetration and thereafter remains almost constant at all fiber contents. The CBR strength and secant modulus of soil have improved significantly with fiber content up to an optimum fiber content value of 0.75%, and decrease with increase in soaking time at any fiber content. The maximum improvement in CBR strength is found out as 2.48, 2, and 1.5 times for 4, 20, and 40 days soaking for 0.75% fiber inclusion. It has been found that the glass fiber-reinforced soil can be extensively used as subgrade material.