Abstract:Dispersion in clay may create problems for civil projects. Dispersive soils are clayey, high in sodium content, and washed easily when subjected to water with low salt concentrations. The current study investigated the use of cellulose nanofibers (CNF) and recycled glass powder (RGP) for dispersive soil stabilization. Different proportions of CNF (0%, 0.5%, 1%, 1.5% and 2% by weight of soil) and RGP (0%, 2%, 4%, 6% and 8% by weight of soil) were added to dispersive soil. The results of the double hydrometer test indicated that combining CNF and RGP significantly decreased the dispersion potential. The greatest decrease in dispersion potential was achieved with the addition of 1.5% CNF plus 6% and 8% RGP, which the soil was classified as non-dispersive. Atterberg limits testing indicated a decrease in the plasticity index. The greatest decrease in PI (41.5%) was achieved with the addition of 1.5% CNF plus 8% RGP to the soil. The results of the density tests on the samples by combining CNF and RGP revealed that the maximum dry density of the soil increases. SEM images showed that calcium silicate hydrate (CSH) gel was formed in samples containing 1.5% CNF and different percentages of RGP. This eventually caused an increase in the unconfined compressive strength. The greatest increase in strength was observed with the combination of 1.5% CNF and 8% RGP. The strength of these samples increased by 5.9, 10.4, and 12.5 times after 7, 14, and 28 days of curing, respectively, compared to the unmodified sample.

Effect of cellulose nanofibers and recycled glass powder on the geotechnical and microstructural parameters of dispersive soil