Effect of Interleaved Electrolyte Forms on Macro-scaled Structural Hybrid Supercapacitors with Asymmetric Configurations of Graphene-coated Carbon Fabric Electrodes
Kuray Dericiler,Marjan Hezarkhani,Isa Emami Tabrizi,Semih Dogan,Ilayda Berktas,Emre Erdem,Suresh G. Advani,Mehmet Yildiz,Hatice S. Sas,Burcu Saner Okan
DOI: https://doi.org/10.1007/s10443-023-10130-y
IF: 2.3
2023-05-09
Applied Composite Materials
Abstract:Structural composites supercapacitors are manufactured by converting commercial carbon fabrics into electrodes by applying a surface treatment without changing their sizing chemistry, integrating electrolytes with single and hybrid material components in the forms of solution, gel, and film, with glass fabrics as a separator to prevent short-circuit in the system. Carbon fabrics are treated by applying stepwise dip-coating method including graphene oxide (GO) coating, Fe 2 O 3 treatment and reduction steps in aqueous medium. Four configured supercapacitors are tested by changing electrodes and electrolytes. Supercapacitor with reduced GO (rGO) and rGO-Fe 2 O 3 coated carbon fabric electrodes with mesoporous PVA-KOH film electrolyte in the laminated structure covered by insulator films demonstrates 46% charge retention at 1 V after 30 s, 21 Ω charge transfer resistance, 120 mWh/kg energy density, 3.12 W/kg power density, and 0.35 mF/g specific capacitance. Electrolytes in gel and solution forms do not display any capacitance behavior in cyclic voltammetry analysis and exhibit lower energy densities compared to the film electrolyte. PVA-KOH film electrolyte provides a synergistic effect with resized commercial grade carbon fabric electrodes through its homogenous impregnation on electrode surfaces which is responsible for the enhancement of charge-storage behavior of the fabricated structural supercapacitors.
materials science, composites