Robust Single‐Walled Carbon Nanotube‐Infiltrated Carbon Fiber Electrodes for Structural Supercapacitors: from Reductive Dissolution to High Performance Devices
Evgeny Senokos,David B. Anthony,Noelia Rubio,Maria Crespo Ribadeneyra,Emile S. Greenhalgh,Milo S. P. Shaffer
DOI: https://doi.org/10.1002/adfm.202212697
IF: 19
2023-02-02
Advanced Functional Materials
Abstract:Hierarchical carbon fiber (CF)/single‐walled carbon nanotube (SWCNT) structural electrodes are produced using reductive chemistry to infiltrate highly individualized nanotubide ions into woven fabrics. This versatile room temperature method introduces SWCNT networks within the CF plies, maximizing electrochemical performance, without causing damage or interrupting fiber packing. The SWCNTs provide high conductivity (2000 S cm−1), surface area (>1000 m2 g−1), and capacitance (101 F g−1). Four different SWCNT sources are evaluated to identify the characteristics that offer the best multifunctional performance for use in composite‐based structural supercapacitors. Multifunctional electrodes for structural supercapacitors are prepared by vacuum infiltration of single‐walled carbon nanotubes (SWCNTs) into woven carbon fibers (CFs); the use of reductive charging chemistry to form nanotubide solutions ensured a high degree of individualization. The route is highly versatile, as shown by comparing four different commercial nanotube feedstocks. In film form, the pure nanotubide networks ("buckypapers") are highly conductive (up to 2000 S cm−1) with high surface area (>1000 m2 g−1) and great electrochemical performance (capacitance of 101 F g−1, energy density of 27.5 Wh kg−1 and power density of 135 kW kg−1). Uniformly integrating these SWCNT networks throughout the CF fabrics significantly increased electrical conductivity (up to 318 S cm−1), surface area (up to 196 m2 g−1), and in‐plane shear properties, all simultaneously. The CNT‐infiltrated CFs electrodes exhibited intrinsically high specific energy (2.6–4.2 Wh kg−1) and power (6.0–8.7 kW kg−1) densities in pure 1‐ethyl‐3‐methylimidazolium bis(trifluoromethylsulfonyl)imide (EMIM TFSI) electrolyte. Multifunctional structural supercapacitors based on CNT‐coated CFs offer a substantial increase in capacitive performance while maintaining the tensile mechanical properties of the as‐received CF‐based composite. This non‐damaging approach to modify CFs with highly graphitic, high surface area nanocarbons provides a new route to structural energy storage systems.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology