Influence of Reactive MgO Hydration and Cement Content on C&DW Aggregate Concrete Characteristics

Ali Heidari,Masoumeh Hashempour,Mehdi Delshad Chermahini

DOI: https://doi.org/10.1007/s40999-018-0361-5

IF: 2.184

2018-10-16

International Journal of Civil Engineering

Abstract:Accumulating construction and demolition waste (C&DW) and the rather high hydration temperature of cement are two problems which affect the environment and mass concrete production, respectively. In this study, the effects of reactive MgO hydration and cement content’s role on the mechanical characteristics of C&DW aggregate concrete were evaluated for finding the suitable solution for solving the above-mentioned problems. In the experimental program, sand to cement ratios of 3 and 2.5 were considered (S/C) and the reactive MgO was 2–6 wt% of cement. Also, two types of experiments such as mechanical and chemical tests were carried out. The compressive strength test showed that by increasing the reactive MgO to 6 wt% of cement, the compressive strength of samples in the S/C of 2.5 is higher than the 3. Also, by increasing the percentage of C&DW aggregate from 30 to 60%, the water absorption of samples increases. In the field emission scanning electron microscopy (FESEM) analysis with cases of 2–6% MgO, 60% C&DW aggregate and S/C of 3, cracks were observed, while they were not detected in samples with S/C of 2.5. The X-ray diffraction (XRD) test, confirmed that the major peak of the patterns in almost every sample was related to calcite and with increase in the MgO content to 6%wt., tricalcium silicate was not formed in both samples with S/C of 2.5 and 3. This study confirm that using C&DW aggregate as concrete is practical for making green concrete and using MgO helps to reduce its hydration temperature.

engineering, civil