In‐situ preparation and electrochromic properties of TiO 2 / PTPA‐HTAN core‐shell nanocomposite film
Mi Ouyang,Dacheng Dai,Xuming Hu,Yuwen Li,Zhangxin Chen,Bowen Tao,Lina Zhang,Weijun Li,Yujie Dong,Ru Bai,Xiaojing Lv,Cheng Zhang
DOI: https://doi.org/10.1002/pol.20210734
IF: 3.046
2021-12-17
Journal of Polymer Science
Abstract:Abstract A new star‐shaped structure conjugated microporous polymers, poly (2,8,14‐tri[4‐diphenyl‐benzene]‐hexaazatrinaphthylene) (PTPA‐HATN), was designed and in‐situ electrochemically polymerized on the surfaces of FTO electrodes with a directional alignment TiO 2 nanorod array to obtain TiO 2 /PTPA‐HATN core‐shell nanocomposite films. Compared with the PTPA‐HATN film, the TiO 2 /PTPA‐HATN composite film exhibits higher optical contrast and faster response time, with contrast of 57% at 783 nm, coloring time of 3.62 s and discoloring time of 2.55 s (43%, 4.63 s and 4.77 s for PTPA‐HATN film, respectively). After 400 cycles, the contrast of nanocomposite film decreased by 28%, while the PTPA‐HATN film basically lost its electrochromic properties. A simple three‐layer EC prototype device based on TiO 2 /PTPA‐HATN nanocomposite film constructed with hydrogel electrolyte clearly shows color changes at different voltages. On the one hand, the formation of core‐shell porous nanostructure of TiO 2 /PTPA‐HATN composite film provides a larger ion doping/de‐doping interface, shortening the average diffusion length of ions. On the other hand, the large indented polymer‐nanorods contact interface makes it difficult for the polymer to detach from the electrode, thus significantly improving the cyclic stability of the composite film.
polymer science