Abstract:dTT is synthesized and its homopolymer (PdTT) is prepared electrochemically.PdTT presents camel, olive green, and dark blue at 0.0, 0.8, and 1.0 V, respectively.P(dTT-co-bTp) reveals high △T (41.3%) and η (149.4 cm2/C) at 1070 nm.P(dTT-co-TF)/PEDOT-PSS ECD exhibits high △T (44.7%) at 680 nm.P(dTT-co-CPdT)/PEDOT-PSS ECD displays high η (656.5 cm2/C) at 686 nm and rapid switching time.A 2,5-di(2-thienyl)thieno[3,2-b]thiophene (dTT)-containing homopolymer (PdTT) and four dTT-containing copolymers (P(dTT-co-bTp (2,2′-bithiophene)), P(dTT-co-TF), P(dTT-co-CPdT) and P(dTT-co-CPdTK)) were polymerized using electrochemical method and their electrochromic switching properties were explored. dTT shows lower onset oxidized potential (Eonset) than that of bTp, conjecturing that dTT displays more extended conjugated degree than that of bTp ring. PdTT film presents camel, olive green, and dark blue at 0.0, 0.8 and 1.0 V, respectively. Colorful-to-colorless switching investigations of polymeric films display that P(dTT-co-bTp) has high △T (41.3% at 1070 nm) and η (149.4 cm2/C at 1070 nm) in 0.2 M LiClO4/ACN/DCM solution. Five dual-layer complementary electrochromic devices based on PdTT, P(dTT-co-bTp), P(dTT-co-TF), P(dTT-co-CPdT) or P(dTT-co-CPdTK) as the anodic layer and PEDOT-PSS as the cathodic layer are assembled. P(dTT-co-TF)/PEDOT-PSS ECD exhibits high △T (44.7% at 680 nm) and satisfactory electrochemical redox stability, while P(dTT-co-CPdT)/PEDOT-PSS ECD displays high η (656.5 cm2/C at 686 nm) and rapid switching time (≤ 0.9 s). On the basis of these findings, the present work offers new structural insights for significant design of large contrast and multicolored electrochromic electrodes.Background: The thieno[3,2-b]thiophene (TT) unit is a fused heterocyclic ring, its coplanar structure and electron-donating ability can enhance carrier transporting properties of polymer chain. A 2,5-di(2-thienyl)thieno[3,2-b]thiophene (dTT) unit displays more extended conjugated degree than that of bTp, it is interesting to explore the multichromic behaviors of five dTT-based polymers and their corresponding ECDs upon applying various potentials.Methods: A dTT-containing homopolymer (PdTT) and four dTT-containing copolymers (P(dTT-co-bTp), P(dTT-co-TF), P(dTT-co-CPdT) and P(dTT-co-CPdTK)) are polymerized using electrochemical method. The spectral properties, kinetic characterizations, open-circuit memory, and electrochemical redox stability of PdTT/PEDOT-PSS, P(dTT-co-bTp)/PEDOT-PSS, P(dTT-co-TF)/PEDOT-PSS, P(dTT-co-CPdT)/PEDOT-PSS and P(dTT-co-CPdTK)/PEDOT-PSS ECDs are systematically studied.Significant Findings: The present work offers new structural insights for significant design of large contrast and multicolored electrochromic electrodes.The dual-layer electrochromic devices were assembled by arranging PdTT, P(dTT-co-bTp), P(dTT-co-TF), P(dTT-co-CPdT), or P(dTT-co-CPdTK) as the anodically coloring electrochromic polymer and PEDOT-PSS as the cathodically coloring electrochromic polymer to face each other, and two electrodes were separated by a PMMA/PC/LiClO4 electrolyte. At 0.0 V, P(dTT-co-TF) was bright camel in its neutral state and PEDOT-PSS was transparent in its oxidized state. Therefore, the P(dTT-co-TF)/PEDOT-PSS ECD was transparent. As the potential increased from 0.0 V to +1.4 V, the color of P(dTT-co-TF) and PEDOT-PSS films became grayish-blue and light blue, respectively. As the potential increased further from +1.4 V to +2.0 V, the color of PEDOT-PSS film became dark blue in its neutral state. The color of P(dTT-co-TF)/PEDOT-PSS ECD was dark blue at +2.0 V. P(dTT-co-TF)/PEDOT-PSS ECD exhibits high △T (44.7% at 680 nm) and satisfactory long-term cycling stability.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1876107021003321-fx1_lrg.jpg">Download : Download high-res image (105KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1876107021003321-fx1.jpg">Download : Download full-size image</a></li></ol>

Unsubstituted Polythiophene Film Deposited via In-Situ Sequential Solution Polymerization for Chemo-/Electrochromism

Color combination of polythiophene films doped with three dye molecules for electrochromism

Electrochromic Properties of Polymers/Copolymers Via Electrochemical Polymerization Based on Star-Shaped Thiophene Derivatives with Different Central Cores

Electropolymerized Thiophene-Based Polymer with Pure Donor System Enable Magenta-to-transmissive Electrochromic-Supercapacitor Bifunctional Material

Preparation of Multicolor Electrochromic Polymer Composite Film with Laminated Structure

Liquid/Liquid Interfacial Suzuki Polymerization Prepared Novel Triphenylamine-Based Conjugated Polymer Films with Excellent Electrochromic Properties

Quadruple Thiophene Based Electrochromic Electrodeposited Film As High Performance Hybrid Energy Storage System

Electrochromic polymers based on 2,5-di(thiophen-2-yl)thieno[3,2-b]thiophene and thiophene derivatives as potential anodic layers for high performance electrochromic devices

Design Strategy For Efficient Solution-Processable Red Electrochromic Polymers Based On Unconventional 3,6-Bis(Dodecyloxy)Thieno[3,2-B]Thiophene Building Blocks

4-(Trifluoromethoxy)phenyl-Containing Polymers as Promising Anodic Materials for Electrochromic Devices

Controlled Synthesis of Poly[(3-alkylthio)thiophene]s and Their Application to Organic Field-Effect Transistors

Colorless to Multicolored, Fast Switching, and Highly Stable Electrochromic Devices Based on Thermally Cross-Linking Copolymer

Multichromic Polymers Containing Alternating Bi(3-Methoxythiophene) and Triphenylamine Based Units with Para-Protective Substituents

Exploring the electrochromic properties of poly(thieno[3,2-: B] thiophene)s decorated with electron-deficient side groups

Color Combination Of Polysiloxane Polymer By Introducing Two Different Triphenylamine Based Pendent Groups For Electrochromism

Solution-Processable Neutral Green Electrochromic Polymer Containing Thieno[3,2-b]thiophene Derivative As Unconventional Donor Units

Synthesis and characterization of a liquid-like polythiophene and its potential applications

Electrochromic Kinetics of Nanostructured Poly(3,4-(2,2-dimethylpropylenedioxy)thiophene) Film on Plastic Substrate

Multi-color poly(3-methylthiophene) films prepared by a novel pre-nucleation electrodeposition grown method for enhancing electrochromic stability

Thermally Cross-Linked Copolymer for Highly Transparent to Multicolor-Showing Electrochromic Materials

Electrochemistry of some β‐Substituted Polythiophenes: Anodic Oxidation, Electrochromism, and Electrochemical Deactivation