Abstract:dTT is synthesized and its homopolymer (PdTT) is prepared electrochemically.PdTT presents camel, olive green, and dark blue at 0.0, 0.8, and 1.0 V, respectively.P(dTT-co-bTp) reveals high △T (41.3%) and η (149.4 cm2/C) at 1070 nm.P(dTT-co-TF)/PEDOT-PSS ECD exhibits high △T (44.7%) at 680 nm.P(dTT-co-CPdT)/PEDOT-PSS ECD displays high η (656.5 cm2/C) at 686 nm and rapid switching time.A 2,5-di(2-thienyl)thieno[3,2-b]thiophene (dTT)-containing homopolymer (PdTT) and four dTT-containing copolymers (P(dTT-co-bTp (2,2′-bithiophene)), P(dTT-co-TF), P(dTT-co-CPdT) and P(dTT-co-CPdTK)) were polymerized using electrochemical method and their electrochromic switching properties were explored. dTT shows lower onset oxidized potential (Eonset) than that of bTp, conjecturing that dTT displays more extended conjugated degree than that of bTp ring. PdTT film presents camel, olive green, and dark blue at 0.0, 0.8 and 1.0 V, respectively. Colorful-to-colorless switching investigations of polymeric films display that P(dTT-co-bTp) has high △T (41.3% at 1070 nm) and η (149.4 cm2/C at 1070 nm) in 0.2 M LiClO4/ACN/DCM solution. Five dual-layer complementary electrochromic devices based on PdTT, P(dTT-co-bTp), P(dTT-co-TF), P(dTT-co-CPdT) or P(dTT-co-CPdTK) as the anodic layer and PEDOT-PSS as the cathodic layer are assembled. P(dTT-co-TF)/PEDOT-PSS ECD exhibits high △T (44.7% at 680 nm) and satisfactory electrochemical redox stability, while P(dTT-co-CPdT)/PEDOT-PSS ECD displays high η (656.5 cm2/C at 686 nm) and rapid switching time (≤ 0.9 s). On the basis of these findings, the present work offers new structural insights for significant design of large contrast and multicolored electrochromic electrodes.Background: The thieno[3,2-b]thiophene (TT) unit is a fused heterocyclic ring, its coplanar structure and electron-donating ability can enhance carrier transporting properties of polymer chain. A 2,5-di(2-thienyl)thieno[3,2-b]thiophene (dTT) unit displays more extended conjugated degree than that of bTp, it is interesting to explore the multichromic behaviors of five dTT-based polymers and their corresponding ECDs upon applying various potentials.Methods: A dTT-containing homopolymer (PdTT) and four dTT-containing copolymers (P(dTT-co-bTp), P(dTT-co-TF), P(dTT-co-CPdT) and P(dTT-co-CPdTK)) are polymerized using electrochemical method. The spectral properties, kinetic characterizations, open-circuit memory, and electrochemical redox stability of PdTT/PEDOT-PSS, P(dTT-co-bTp)/PEDOT-PSS, P(dTT-co-TF)/PEDOT-PSS, P(dTT-co-CPdT)/PEDOT-PSS and P(dTT-co-CPdTK)/PEDOT-PSS ECDs are systematically studied.Significant Findings: The present work offers new structural insights for significant design of large contrast and multicolored electrochromic electrodes.The dual-layer electrochromic devices were assembled by arranging PdTT, P(dTT-co-bTp), P(dTT-co-TF), P(dTT-co-CPdT), or P(dTT-co-CPdTK) as the anodically coloring electrochromic polymer and PEDOT-PSS as the cathodically coloring electrochromic polymer to face each other, and two electrodes were separated by a PMMA/PC/LiClO4 electrolyte. At 0.0 V, P(dTT-co-TF) was bright camel in its neutral state and PEDOT-PSS was transparent in its oxidized state. Therefore, the P(dTT-co-TF)/PEDOT-PSS ECD was transparent. As the potential increased from 0.0 V to +1.4 V, the color of P(dTT-co-TF) and PEDOT-PSS films became grayish-blue and light blue, respectively. As the potential increased further from +1.4 V to +2.0 V, the color of PEDOT-PSS film became dark blue in its neutral state. The color of P(dTT-co-TF)/PEDOT-PSS ECD was dark blue at +2.0 V. P(dTT-co-TF)/PEDOT-PSS ECD exhibits high △T (44.7% at 680 nm) and satisfactory long-term cycling stability.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1876107021003321-fx1_lrg.jpg">Download : Download high-res image (105KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1876107021003321-fx1.jpg">Download : Download full-size image</a></li></ol>

Color combination of polythiophene films doped with three dye molecules for electrochromism

Blue/green-to-transmissive Electrochromic-Supercapacitor Bifunctional Polymer Films Via Electropolymerization Containing 3,4-Propylenedioxythiophene Derivatives As Novel Donor Units

Electrochromic Properties of Polymers/Copolymers Via Electrochemical Polymerization Based on Star-Shaped Thiophene Derivatives with Different Central Cores

Electrochemical synthesis and properties of multicolor electrochromic triphenylamine-based polymer films

Unsubstituted Polythiophene Film Deposited via In-Situ Sequential Solution Polymerization for Chemo-/Electrochromism

4-(Trifluoromethoxy)phenyl-Containing Polymers as Promising Anodic Materials for Electrochromic Devices

Preparation of Multicolor Electrochromic Polymer Composite Film with Laminated Structure

Synthesis and characterization of D-A type electrochromic polymers based on planar monomers: Cyclopenta[2,1-b;3,4-b′]dithiophene and tris(thienothiophene) as electron donors, diketopyrrolopyrrole as electron acceptor

Effects of Chemical Composition, Film Thickness, and Morphology on the Electrochromic Properties of Donor-Acceptor Conjugated Copolymers Based on Diketopyrrolopyrrole

Electrochromic polymers based on 2,5-di(thiophen-2-yl)thieno[3,2-b]thiophene and thiophene derivatives as potential anodic layers for high performance electrochromic devices

Exploring the electrochromic properties of poly(thieno[3,2-: B] thiophene)s decorated with electron-deficient side groups

Multielectrochromic Copolymers of 3,4-Ethylenedioxythiophene and Naphthalene Prepared Via Electropolymerization in Boron Trifluoride Diethyl Etherate

Applications of polymer coatings consisting of 9,9′-(4,4′-sulfonylbis(4,1-phenylene))biscarbazole and thiophene derivatives in electrochromic devices

Electrochromic Properties of Methylol Modified Poly (3, 4-Propylenedioxythiophene) and Its Copolymer with Poly (3, 4-Ethylenedioxythiophene)

Electropolymerized Thiophene-Based Polymer with Pure Donor System Enable Magenta-to-transmissive Electrochromic-Supercapacitor Bifunctional Material

D‐A type hybrid polymers based on EDOT and various benzodiazoles for electrochromic materials

Fine-tuning the color hue of the solution-processable electrochromic copolymers based on the diketopyrrolopyrrole, benzodithiophene and dithienosilole units

High-performance fluorinated D-A-D type electrochromic polymers with different structural types of thiophene donor units

Achieving the gray to transparent switching electrochromic properties based on the diketopyrrolopyrrole, 3,4-propylenedioxythiophene and thieno[3,2-b]thiophene units

Colorless to Multicolored, Fast Switching, and Highly Stable Electrochromic Devices Based on Thermally Cross-Linking Copolymer

Design of Dithienopyran-Based Conjugated Polymers for High-Performance Electrochromic Devices