Abstract:Composites consisting of rhodium, copper, and copper-rhodium nanoparticles (2 nm in average diameter) dispersed in a high-surface area graphite powder (~ 10 wt.% of metal) have been synthesized by a wet chemical method. After characterization by ICP-OES and TEM, they have been tested for the electrochemical reduction of nitrates in alkaline media (10−1 mol L−1 KOH) using a cavity microelectrode. It is found that in the 0.02–0.5 V/RHE potential range, bimetallic composites exhibit a much higher electrocatalytic activity than single-metal composites. The peak current describes a volcano plot as a function of the composition, with a maximum for CuRh, which is 7.5 times higher than that obtained with pure rhodium (under identical metal wt.%). This synergistic effect can be rationalized directly from the electrochemical response of pure metals. It is then tentatively attributed to the fact that the first (rate determining) reduction step, corresponding to the formation of nitrites, takes place efficiently in copper-rich areas while the subsequent steps of nitrite reduction in ammonia (via hydroxylamine formation) occur in rhodium-rich areas. For the same mass of rhodium, the electrocatalytic conversion of nitrates to ammonia is 12 times more effective with CuRh than with pure rhodium. With the additional gain in active surface area due to the nanoparticle morphology compared to bulk or thin film forms, these results represent a step-forward in cost reduction of rhodium-based electrocatalysts for the conversion of nitrates to ammonia.Graphical AbstractComposites of copper-rhodium nanoparticles in graphite powder were tested for the electrochemical reduction of nitrates in alkaline media. They exhibit a much higher electrocatalytic activity for the conversion of nitrates to ammonia than composites with pure rhodium nanoparticles, up to 12 times more at a composition close to CuRh.

Interfacial Engineering Enhances the Electroactivity of Frame‐Like Concave RhCu Bimetallic Nanocubes for Nitrate Reduction

Accelerating Electrocatalytic Nitrate Reduction to Ammonia Via Weakening of Intermediate Adsorption on Cu-Based Catalyst

Carbon Nanocage Confining CuCo Bimetallic Interface with Low Nitrate Adsorption Energy for Highly Efficient Electrochemical Ammonia Synthesis

Electronic Metal–Support Interaction Triggering Interfacial Charge Polarization over CuPd/N‐Doped‐C Nanohybrids Drives Selectively Electrocatalytic Conversion of Nitrate to Ammonia

Dynamically Restructuring Nanoporous Cu-Co Electrocatalyst for Efficient Nitrate Electroreduction to Ammonia

Electrocatalytic Reduction of Nitrate/Nitrite to Ammonia on CuCo Nanoparticles Decorated N‐doped Carbon

Interface coupling of Ni 2 P@Cu 3 P catalyst to facilitate highly-efficient electrochemical reduction of nitrate to ammonia

Fe/Cu diatomic catalysts for electrochemical nitrate reduction to ammonia

Mixed-valence Cu-based heterostructures for efficient electrochemical nitrate reduction to ammonia

Heterogenous Cu@ZrO2 nanofibers enable efficient electrocatalytic nitrate reduction to ammonia under ambient conditions

Efficient Electrochemical Nitrate Reduction to Ammonia with Copper-Supported Rhodium Cluster and Single-Atom Catalysts

Dual Enhancement of Cu 2 S/CuO Nanocomposites in N-Doped Porous Carbon for Highly Efficient Electrochemical Nitrate Reduction to Ammonia

Electrocatalytic Reduction of Nitrate and Nitrite at CuRh Nanoparticles/C Composite Electrodes

Enhanced electrocatalytic reduction of nitrate over a ternary alloy catalyst of CuPdFe: Structure, performance, and mechanism

Enhanced ammonia selectivity on electrochemical nitrate reduction: Cu–Ni metal–organic frameworks with tandem active sites for cascade catalysis

Electrochemical Nitrate Reduction to Ammonia on CuCo Nanowires at Practical Level

Surface Structure Reformulation from CuO to Cu/Cu(OH)2 for Highly Efficient Nitrate Reduction to Ammonia

Enhancing Electrochemical Nitrate Reduction to Ammonia over Cu Nanosheets Via Facet Tandem Catalysis

One Bicopper Complex with Good Affinity to Nitrate for Highly Selective Electrocatalytic Nitrate Reduction to Ammonia

Nano-Polycrystalline Cu Layer Interlaced with Ti3+-Self-Doped TiO2 Nanotube Arrays as an Electrocatalyst for Reduction of Nitrate to Ammonia

Metal–organic framework-derived Cu nanoparticle binder-free monolithic electrodes with multiple support structures for electrocatalytic nitrate reduction to ammonia