Abstract:TiAl intermetallic compounds, as a new kind of high-performance light-weight structural material, are widely applied in many fields. Titanium carbide (TiC) as the reinforcing phase could improve the mechanical properties, wear resistance, and heat-resistance stability of TiAl intermetallic compounds. Ti(Al, C) mixture powders were deposited by cold spraying at gas temperature of 250 °C, 450 °C, and 550 °C. Then, Ti(Al, C) coatings were annealed at temperatures of 650 °C for different times and following holding at 1100 °C for 3 h. The microstructure, microhardness, fracture toughness, and abrasive wear of Ti-Al composite coatings were investigated. The research results were that the particle size of mixture powders decreased as the ball milling time prolonging. Ti(Al) solid solution appeared in the mixture powders as the milling time increased to 30 h. The average porosity of the coating sprayed at 550 °C was the lowest (0.85%). The as-sprayed coatings exhibited the same phase compositions with the mixture powders. The coating sprayed at gas temperature of 550 °C has the highest microhardness and the lowest weight loss. Ti-Al intermetallic was in-situ synthesized after annealing at 650 °C. The average porosity of the annealed coating (sprayed at 450 °C) was the lowest. The content of Ti-Al intermetallic compounds of the annealed coating sprayed at 450 °C is the highest. The X-ray diffraction (XRD) analysis results are consistent with the EDS analysis of the annealed coatings after annealing at 650 °C. Ti-Al intermetallic compounds were almost completely formed in the three kinds of the coatings after annealing at 650 °C for 20 h and following holding at 1100 °C for 3 h. TiAl and TiAl3 intermetallic phases were in-situ synthesized in the coatings based on the energy dispersive spectroscopy (EDS) and XRD analysis. TiC was also in situ synthesized in the coatings as the annealing temperature increased to 1100 °C. The annealed coating (sprayed at 450 °C) has the highest microhardness, fracture toughness, and wear resistance properties after annealing at 1100 °C for 3 h.

Surface strengthening aluminum alloy by in-situ TiC-TiB2 composite coating

In-situ TiB2-TiC reinforced Fe-Al composite coating on 6061 aluminum alloy by laser surface modification

Microstructure, Microhardness, Fracture Toughness, and Abrasive Wear of In-Situ Synthesized TiC/Ti-Al Composite Coatings by Cold Spraying Combined with Heat Treatment

Improved Wear Resistance and Mechanical Properties of Al Matrix with TiAl-based Coatings

Effects of Aluminum Addition on Microstructure and Properties of TiC-TiB2/Fe Coatings In Situ Synthesized by TIG Cladding

Metallurgical Synthesis of TiC/Al3Ti Surface Composite Coating

Microstructure and high-temperature wear properties of in situ TiC composite coatings by plasma transferred arc surface alloying on gray cast iron

In-situ Synthesized TiC-TiB2 Composite Coatings Prepared by Laser Cladding

The in Situ Synthesis and Wear Performance of a Metal Matrix Composite Coating Reinforced with TiC–TiB2 Particulates, Formed on Ti–6Al–4V Alloy by a Low Oxygen Partial Pressure Fusing Technique

An Ultra-Hard and Thick Composite Coating Metallurgically Bonded to Ti–6Al–4V

Enhanced Interfacial Bonding and Superior Oxidation Resistance of CoCrAlY-TiB2 Composite Coating Fabricated by Air Plasma Spraying

Microstructure evolution and mechanical properties of TIG cladded TiB reinforced composite coating on Ti-6Al-4V alloy

Preparation of in-situ synthesized TiC/AlSi30Cu5 coating by high velocity oxy-fuel (HVOF) spraying: Microstructure evolution, mechanical properties, and tribological behavior

A novel approach to coating for improving the comprehensive high-temperature service performance of TiAl alloys

Enhancing the hardness and wear resistance of a TiC-Ni composite coating on grade 2 pure titanium by electron beam remelting

Electron Beam Surface Alloying of Γ-Tial Intermetallic Alloy for Ti5Si3/TiAl Composite Coatings

Fabrication of Thermal Resistant Surface Composite Coating on Cast Steel

Friction and wear performance of in-situ synthesized TiC composite strengthened coating on gray cast iron

Intergrowth Microstructure and Superior Wear Resistance of (tib + TiC)/Ti64 Hybrid Coatings by Gas Tungsten Arc Cladding

Two-scale TiB/Ti64 Composite Coating Fabricated by Two-Step Process

Tuning composition and microstructure by doping Ti and C for enhancing mechanical property and wear resistance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloy matrix composites