Dolomite-derived composites doped with binary ions for direct solar thermal conversion and stabilized thermochemical energy storage
Shengbin Bai,Jian Sun,Lei Liu,Yun Da,Zijian Zhou,Ruiling Wang,Yafei Guo,Chuanwen Zhao
DOI: https://doi.org/10.1016/j.solmat.2022.111659
IF: 6.9
2022-06-01
Solar Energy Materials and Solar Cells
Abstract:Thermochemical energy storage (TCES) via the calcium looping (CaL) process is an emerging technology applied in third-generation concentrated solar power plants. A range of CaO-based composites was developed via binary Fe and Mn ions doping of low-cost dolomite for direct solar absorption. The doping ratio of Fe and Mn ions was investigated and optimized aiming to produce the highly efficient Fe/Mn-doped, acid-modified dolomite composites. After comprehensively considering the spectral absorptance and energy storage density, the composite with a molar ratio of Ca/Mg:Mn:Fe=100:2:4 is optimal. It possesses a relatively high spectral absorptance of 63.7% due to the generated, dark Ca-Mn-Fe oxides, which is up to ∼2.1 times higher than that of raw dolomite. Moreover, the composite exhibits excellent cycling stability (a gravimetric energy storage density loss of ∼6.6% after 30 cycles) resulting from uniformly distributed, intrinsic MgO grains. Additionally, dolomite-derived composite pellets were prepared using extrusion-spheronization, and their volumetric energy density is remarkably superior to that of the powder, ∼2.37 GJ/m3 after 30 cycles. The fresh pellets (7.25± 0.64 MPa) and calcined pellets (3.19 ± 0.29 MPa) both possess desirable ability to resist mechanical stress and thermal shock. Therefore, Fe/Mn-doped, dolomite-derived composite pellets are potential candidates for direct solar absorption when applied in CaL-based TCES systems due to their simultaneously desirable spectral absorbance and cycling stability.
materials science, multidisciplinary,physics, applied,energy & fuels