Abstract:Abstract Development of novel methods to obtain highly active catalysts for photocatalytic hydrogen evolution is desired. This work reports a facile preannealing‐quenching strategy to synthesize oxygen vacancy‐rich anatase TiO 2 hollow spheres. TiO 2 hollow spheres are first synthesized via a versatile kinetics‐controlled coating method and then subjected to high temperature preannealing followed by rapid quenching in liquid‐nitrogen (−196 °C). The as‐quenched samples appear light grey suggesting the presence of abundant surface oxygen vacancies, which are subsequently confirmed by the comprehensive analyses of XRD, XPS and EPR spectra. The oxygen vacancies induced by quenching process are proved to have promoted the light adsorption and inhibited the recombination of photo‐induced charges for TiO 2 hollow spheres, which obviously improve the photocatalytic performance of those samples. The results showed that the TiO 2 hollow spheres quenched at 500 °C exhibited a robust stability and the most excellent photocatalytic performance for hydrogen evolution (413.5 μmol h −1 ) over other quenched samples and it displayed 1.51 times higher performance than that of samples normally cooled at 500 °C (273.7 μmol h −1 ). Herein, this liquid‐nitrogen quenching strategy presented here provides an effective route for the synthesis of high‐performance TiO 2 for water splitting and have a promising prospect in the other application.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the efficiency of photocatalytic hydrogen production. Specifically, the author synthesized oxygen - vacancy - rich anatase TiO2 hollow spheres through a simple pre - annealing - quenching strategy. This method aims to enhance the light - absorption ability of the material and suppress the recombination of photogenerated charges by increasing surface oxygen vacancies, thereby significantly improving the photocatalytic performance.
### Research Background
With the increase in energy demand and the intensification of climate change, photocatalytic water - splitting for hydrogen production has received extensive attention as a clean and sustainable energy production method. Since its discovery by Fujishima and Honda in 1971, TiO2 - based materials have been widely used in photocatalytic hydrogen production due to their abundant resources, non - toxicity, high activity, and stability. However, TiO2 - based materials still have the problem of low photocatalytic efficiency, mainly because of their narrow spectral absorption range and fewer active sites. Therefore, the development of TiO2 - based photocatalysts with abundant active sites and efficient visible - light response has become the focus of research.
### Solution
This paper proposes a method for synthesizing oxygen - vacancy - rich anatase TiO2 hollow spheres through a liquid - nitrogen quenching process. The specific steps are as follows:
1. **Precursor Preparation**: First, an amorphous TiO2 layer is deposited on the surface of silica (SiO2) spheres through a kinetic - control coating method to form a SiO2@TiO2 core - shell structure.
2. **Pre - annealing Treatment**: The SiO2@TiO2 precursor is pre - annealed at a high temperature.
3. **Liquid - nitrogen Quenching**: The pre - annealed sample is quickly immersed in liquid nitrogen (- 196°C) for quenching treatment to generate oxygen - vacancy - rich TiO2 hollow spheres.
4. **Template Removal**: The SiO2 core is removed by etching with NaOH solution to obtain the final TiO2 hollow spheres.
### Experimental Results
- **Structure and Morphology Analysis**: Through SEM, TEM, HRTEM, and XRD characterization, it was confirmed that the structure and morphology of the TiO2 hollow spheres remained unchanged during the quenching process, but the quenched sample showed a lighter color, indicating the formation of surface oxygen vacancies.
- **Spectral Analysis**: XPS, EPR, and Raman spectroscopy further confirmed the formation of oxygen vacancies during the quenching process. In particular, the EPR spectrum showed that the signal intensity of oxygen vacancies in the quenched sample was significantly higher than that in the sample cooled at room temperature.
- **Photocatalytic Performance**: The quenched sample (QH - 500) performed significantly better than the sample cooled at room temperature (NH - 500) in photocatalytic hydrogen production, with a hydrogen production rate reaching 1240.5 μmol, which was 1.52 times higher than that of NH - 500. In addition, QH - 500 also showed excellent stability and photocurrent response.
### Conclusion
The oxygen - vacancy - rich anatase TiO2 hollow spheres synthesized through the liquid - nitrogen quenching process significantly improve the efficiency of photocatalytic hydrogen production. These oxygen vacancies not only enhance the light - absorption ability but also suppress the recombination of photogenerated charges, thereby significantly improving the photocatalytic performance. This method is simple and easy to implement and has broad application prospects.
### Formula Display
- **Hydrogen Production Rate**:
\[
\text{Hydrogen Production Rate}=\frac{\text{Hydrogen Production}}{\text{Time}}=\frac{1240.5\,\mu\text{mol}}{3\,\text{h}} = 413.5\,\mu\text{mol}\cdot\text{h}^{-1}
\]
- **Photocurrent Density**:
\[
\text{Photocurrent Density}=\frac{\text{Photocurrent}}{\text{Electrode Area}}
\]
Hope this information is helpful to you! If you have any other questions or need further explanation, please feel free to let me know.