Microstructure, mechanical properties, and corrosion resistance of continuous heating aging 6013 aluminum alloy

Guopeng Lei,Bo Wang,Jing Lu,Chen Wang,Yimin Li,Fenghua Luo

DOI: https://doi.org/10.1016/j.jmrt.2022.02.101

IF: 6.267

2022-05-01

Journal of Materials Research and Technology

Abstract:In this study, the effects of continuous heating aging on the microstructure, mechanical properties, and corrosion resistance of a 6013 aluminum alloy were investigated through tensile, intergranular corrosion, and electrochemical tests. The lattice characterization of precipitates and the grain boundaries were analyzed via TEM and HRTEM. The test results indicated that with increasing final aging temperature at a constant heating rate, the alloy strength increased and the intergranular corrosion depth of the alloy decreased. Precipitates formed at the beginning of the aging period were labeled GP I, and the intracrystalline precipitates formed at the peak aging period were labeled GP II. In the over aging period, the precipitates coarsened and their quantity deteriorated; further, the Q′ phase appeared during the over aging period. The size and span of the grain boundary precipitates increased with increasing final aging temperature, and the PFZ width decreased with increasing heating rate. After continuous heating aging from 120 °C to 220 °C at a heating rate of 60 °C/h, the intergranular corrosion depth of the alloy was only 94.2 μm, whereas it was 152.1 μm after the T6 process. Thus, it was determined that the sensitivity of the intergranular corrosion of alloys depends on the grain boundary structure.