Humidity-independent gas sensor based on Pt/SnO 2 /NiO with advanced CO sensing capabilities
Saisai Zhang,Mingli Xing,Yi Zheng,Bowen Zhang,Na Luo,Yan Wang,Zhanying Zhang
DOI: https://doi.org/10.1016/j.jallcom.2024.177712
IF: 6.2
2024-11-28
Journal of Alloys and Compounds
Abstract:Aimed at realizing the sensors capable of functioning effectively in high-humidity environments, the Pt/SnO 2 /NiO ternary composite materials featuring noble metal and p-n heterojunction structures was synthesized. The dispersion of SnO 2 and Pt nanoparticles on NiO nanosheets was found to be excellent, resulting in a nearly twofold increase (99.45 m 2 g −1 of Pt/SnO 2 /NiO) in specific surface area compared to pure NiO materials (51.977 m 2 g −1 ). The CO sensitivity tests revealed that, in contrast to pure NiO sensors (with an optimal operating temperature of 290°C), Pt/SnO 2 /NiO ternary composites exhibited an optimal operating temperature (OOT) of 270°C, a decrease of 20°C for CO detection at a relative humidity of 22 %. At this OOT, Pt/SnO 2 /NiO sensors consistently displayed high responsiveness (2.5 times higher than that of the pure NiO sensor), good selectivity, and rapid response-recovery times (the recovery time is reduced by nearly half compared to that of the pure NiO sensor). Furthermore, the sensors' responses to CO under different humidity conditions (from 22 % to 91 %) at 270°C were investigated. The results demonstrated that Pt/SnO 2 /NiO sensors exhibited minimal variation in their response to CO at a range of relative humidity levels (41.5 % at 91 %, 39.5 % at 22 %, respectively). These results highlight that the enhancement of CO gas sensitivity in the sensors primarily results from the high catalytic activity of noble metal Pt and the p-n heterojunction interaction.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering