Abstract:In order to achieve the purpose of regulating the pore structure characteristics of activated carbon by adjusting the experimental parameters, the effects of carbonization temperature, carbonization time, pre-activation temperature, pre-activation time and impregnation time on the pore structure of sargassum-based activated carbon (SAC) are studied by orthogonal experiment. The gravimetric capacitance of SAC and the relationship between the gravimetric capacitance and specific surface area are also studied. The results show that the SACs prepared at all experimental conditions have developed pore structure and huge specific surface area, reaching 3,122 m 2 /g. The pore size of SAC is almost all within 6 nm, in which the micropores are mainly concentrated in 0.4–0.8 nm, the mesopores are mainly concentrated in 2–4 nm, and the number of micropores is significantly higher than that of mesopores. During the preparation of SAC, the effect of carbonization temperature on the specific surface area and specific pore volume of SAC is very significant. The effect of carbonization time on the specific surface area of SAC is significant, but the effect on specific pore volume can be ignored. The effects of pre-activation temperature, pre-activation time, and impregnation time on specific surface area and specific pore volume of SAC can be ignored. In addition, SACs show good gravimetric capacitance performance as electrode material for supercapacitors, which can significantly increase the capacitance of supercapacitors and thus broaden their applications. The gravimetric capacitance and specific surface area of SACs show a good linear relationship when the activated carbons have similar material properties and pore size distribution.

The performance of sulphur doped activated carbon supercapacitors prepared from waste tea

Preparation and Electrochemical Properties of PF-based Activated Carbon

Preparation of N-, S-Co-Doped Activated Carbons Derived from Waste Medium Density Fiberboard for Supercapacitors

Mesoporous structure favorable for high voltage and high energy supercapacitor based on green tea waste-derived activated carbon

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Activated carbon from the waste water purifier for supercapacitor application

Enhancing the pore wettability of coal-based porous carbon as electrode materials for high performance supercapacitors

Regeneration and usage of commercial activated carbon from the waste electrodes for the application of supercapacitors

Preparation of a N-P co-doped waste cotton fabric-based activated carbon for supercapacitor electrodes

High‐performance activated carbons for supercapacitor: Effects of porous structures, heteroatom doping, and morphology

Transforming waste sugar solution into N-doped hierarchical porous carbon for high performance supercapacitors in aqueous electrolytes and ionic liquid

Acid-treated waste sisal fiber derived activated carbon as efficient electrode material for solid-state supercapacitor

Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor

A new biomass derived rod-like porous carbon from tea-waste as inexpensive and sustainable energy material for advanced supercapacitor application

Pore Structure Regulation and Electrochemical Performance Characterization of Activated Carbon for Supercapacitors

Sulfurized activated carbon for high energy density supercapacitors

Performance of activated carbons synthesized from fruit dehydration biowastes for supercapacitor applications

Different pretreatment methods combined with subsequent activation to convert waste eucalyptus bark into porous carbon electrode materials for supercapacitors

Influence of pore structure on the electrochemical performance of activated carbon as electrode material for aqueous supercapacitors

Hydrothermal Carbonization of Cellulose with Ammonium Sulfate and Thiourea for the Production of Supercapacitor Carbon

Self-templating synthesis of hierarchical porous carbon with multi-heteroatom co-doping from tea waste for high-performance supercapacitor