Synthesis and characterization of optically transparent nickel oxide nanoparticles as a hole transport material for hybrid perovskite solar cells

Kalpana Deevi,Venkata Subba Reddy Immareddy

DOI: https://doi.org/10.1007/s10854-019-00927-8

2019-02-18

Abstract:<h3 class="a-plus-plus">Abstract</h3> <p class="a-plus-plus">Nickel oxide (NiO) nanoparticles are synthesized to use as a transparent ‘hole’ transport material for the fabrication of semi-transparent hybrid perovskite solar cells. The low temperature annealed metal deficit nickel oxide nanoparticles are black in colour and show a significant absorption in the visible region. The near stoichiometric NiO nanoparticles are obtained by high temperature annealing at 700 °C and are nearly optically transparent. X-ray diffraction studies reveal that as obtained NiO nanoparticles are in face centered cubic phase irrespective of their annealing temperatures. The observed black to transparent nature of NiO is attributed to the extent of ‘Ni<sup class="a-plus-plus">3+</sup>’ defects. The morphological study by transmission electron microscopy shows that the transparent NiO nanoparticles are nearly spherical in shape with a size distribution of around 50 nm. The absorbance studies using UV–Vis–NIR spectroscopy reveal that the high temperature annealed NiO nanoparticles have a direct band gap of 3.81 eV whereas the black NiO has the band gap of 3.41 eV. Using ultraviolet photoelectron spectroscopy the ‘energy band structure’ of transparent NiO nanoparticles is determined. As obtained transparent NiO nanoparticles are successfully demonstrated as a ‘hole’ transport material for the fabrication of hybrid perovskite solar cells and realized a photoconversion efficiency of 3.45%.</p>