Comparison on the microstructure, bending properties and tribological behaviors of rail materials treated by laser dispersed quenching and induction assisted laser dispersed quenching
Li Meng,Chen Xian,Beibei Zhu,Rui Yan,Qianwu Hu,Xiaoyan Zeng,Dengzhi Wang
DOI: https://doi.org/10.1016/j.surfcoat.2021.126936
IF: 4.865
2021-03-01
Surface and Coatings Technology
Abstract:<p>Laser dispersed quenching technology (LDQ), which can get composite structure with martensite hardening arrays embedded in the untreated matrix on rail surface, can improve the rail' s wear resistance while not threaten its service safety, thus has attracted a lot of notices recently. However, the severe spalling appearing at quenched zones due to the low toughness of martensite structure therein may reduce the rail's ride-ability and rolling contact fatigue (RCF) life. In view of above problems, an induction assisted laser dispersed quenching technology (IA-LDQ) was proposed to adjust the microstructure and mechanical properties of the quenched zones in this paper. The microstructure and hardness of the quenched zones treated by IA-LDQ with different induction heating temperature (T), and their effects on the bending properties and tribological behaviors of rail materials were studied systemically. Results indicated that the microstructure of the quenched zones changed significantly with the increase of T in IA-LDQ, mixed structure of pearlite + bainite with HV399 and approximate pure pearlite structure with HV377 could be obtained at <em>T</em> = 450 °C and <em>T</em> = 500 °C, respectively. Compared with the rail material treated by LDQ, the bending resistances of rail materials treated by IA-LDQ were enhanced significantly, and that treated by IA-LDQ with <em>T</em> = 450 °C showed the best bending performance. On the other hand, the surface damages such as the vertically extended cracks and severe spalling appearing at the LDQ treated zones could be eliminated by IA-LDQ significantly. By IA-LDQ with <em>T</em> = 400 °C and 450 °C, the rail rollers' resistance to wear and fatigue could be balanced best, in which the wear rates were decreased by 59.7% and 41.3% than the untreated rail substrate, respectively, but the surface damage characteristics were kept almost unchanged. Thus, the IA-LDQ technology shows the potential to hardface the rail.</p>
physics, applied,materials science, coatings & films