Abstract:In this study, a hot isostatic pressing (HIP) manufactured SiC particles (SiC p ) reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite was fabricated through ball-milling, HIP, homogenization, hot extrusion, solution treatment, and aging treatment. The results showed the presence of an interfacial reaction layer, MgAl 2 O 4 , around the SiC p , which enhanced the bonding between the particles and the matrix. The aging treatment resulted in the formation of different aging precipitates, which were featured by GP zone for T4, GP zone + η' (metastable MgZn 2 ) + η (stable MgZn 2 ) for T6 and GP zone + η' (metastable MgZn 2 ) for T6I4. The composite samples of T4, T6, and T6I4 exhibited different mechanical properties. Specifically, the elastic modulus was measured as 102.9, 103.4, and 102.3 GPa, the yield strength was 685.3, 598.1, and 619.7 MPa, the ultimate tensile strength was 713.6, 618.9, and 633.3 MPa, and the elongation was 2.2%, 1.8%, and 2.8%, respectively. Furthermore, the corrosion behavior of the composite was evaluated through electrochemical, intergranular corrosion, and exfoliation corrosion. The corrosion current density was found to be 3.17 × 10 −7 , 4.97 × 10 −7 , and 3.67 × 10 −7 A cm −2 , the corrosion potential was measured as −0.70, −0.81, and −0.56 V, and the maximum intergranular corrosion depth was 139.9, 167.8, and 106.2 μm for T4, T6, and T6I4, respectively. The severity of exfoliation corrosion varied, with T4 showing severe pitting, T6 exhibiting moderate pitting, and T6I4 displaying slight pitting. The strengthening mechanism and load transfer strengthening of the composites were discussed in detail based on theoretical calculations, and the anti-corrosion mechanisms were also analyzed.

Heat Treatable Al‐Zn‐Mg‐Cu Matrix Composites Reinforced With Ni‐Based Metallic Glass Powder

Effect of Precipitation Heat Treatment on a Mechanically Alloyed Al‐Based Composite Reinforced with Metallic Glassy Powder

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

Microstructure and Mechanical Properties of the AlCrFeCoNip/AZ91D Composites After Heat Treatment

Effects of heat treatment on mechanical properties and degradation behavior of hollow glass microsphere reinforced Mg-15Al-5Zn-1.5Cu composites

Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites

Effect of heat treatment on the microstructure, mechanical properties and fracture behaviors of ultra-high-strength SiC/Al–Zn–Mg–Cu composites

Investigation of Microstructures and Mechanical Properties of SiC/AA2024 Nanocomposites Processed by Powder Metallurgy and T6 Heat Treatment

Strength–Plasticity Relationship and Intragranular Nanophase Distribution of Hybrid (GNS + SiCnp)/Al Composites Based on Heat Treatment

Mechanical and corrosion properties of Ti-Ni-Cu-Zr metallic glass matrix composites

Precipitation behavior and mechanical properties of Al-Zn-Mg-Cu matrix nanocomposites: Effects of SiC nanoparticles addition and heat treatment

Formation of Nanoscale Metallic Glassy Particle Reinforced Al-Based Composite Powders by High-Energy Milling

Concurrently achieving strength-ductility combination and robust anti-wear performance in an in-situ high-entropy bulk metallic glass composite

Age-hardening behavior of the extruded Al 7075/Mg EW75 composite

Microstructure and properties of a HIP manufactured SiC p reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite

Enhanced mechanical properties of a novel heat resistant Al-based composite reinforced by the combination of nano-aluminides and submicron TiN particles

Hybrid Heat Treatment for Conventionally Treatable Steel Powder Reinforced Age Hardenable Aluminium Alloy Matrix Composites and Mechanical Property Evaluation

Effect of Heat Treatment on Microstructure and Mechanical Properties of Squeeze Cast n SiCp/AZ91D Magnesium Matrix Composites

Effect of reinforcement volume fraction and T6 heat treatment on microstructure, thermal and mechanical properties of mesophase pitch-based carbon fiber reinforced aluminum matrix composites

Plasticity-improved Zr–Cu–Al Bulk Metallic Glass Matrix Composites Containing Martensite Phase

Acquiring Mg-Ag microalloying TiB 2 /Al-4.5Cu composite simultaneously with ultrahigh strength and ductility via optimized salt-metal reaction and multistage heat treatment